辊底式热处理炉辐射管无氧化加热技术及其应用.pdfVIP

第八届燃料炉委员会暨第一届热仿真与控制委员会学术交流会论文集 辊底式热处理炉辐射管无氧化加热技术及其应用 王 敏 （首钢技术研究院，北京 100041） 摘 要：文章阐述了辐射管无氧化加热技术及其在轧钢热处理炉中的应用情况。辐射管无氧化 加热辊底式热处理炉具有温度均匀、自动化程度高，热处理钢板性能稳定，表面质量好等特点，作 为一种高效、污染小的加热方式，辐射管无氧化加热技术在钢铁加热领域将会得到越来越广泛的应 用。 关键词：辊底式热处理炉；辐射管；无氧化加热 Non-oxidation Radiation Heating Technology and Its Application of Roller Hearth Furnace WANG Min (Shougang Research Institute of Technology, Beijing 100041, China ） Abstract: The non-oxidation radiation heating technology and its application of roller hearth furnace for steel heat treatment were expounded in this paper. This kind of technology has many good characters, such as temperature uniformity, and high automation and stable performance of heat treated steel plate and good surface quality and so on. Non-oxidation radiation heating technology is a high efficient and low pollution heating way. Its application range in steel heating area will get more and more widely. Key words: roller hearth furnace; radiant tube; non-oxidation heating 轧钢厂中辊底式热处理炉的用途很广，既可用于棒线材、管材，也可用于板材。国内多数是明 火加热，现代化轧钢厂生产的成品在热处理过程中不允许氧化和脱碳，必须在可控气氛下进行，因 此，出现辐射管间接加热新技术。 现在越来越多的中厚板厂采用辐射管加热无氧化辊底式炉。该炉为连续辊底式，炉内通惰性气 体（一般为氮气，N299.99%）保护，全辐射管加热，辐射管沿炉膛上下两排布置，进炉前要进行表 面抛丸处理，去掉氧化铁皮，以防带入炉内造成炉底辊的结瘤，划伤钢板表面，影响钢板表面质量。 燃烧系统一般采用混合煤气为燃料，自身预热式烧嘴（可预热空气到 800 ℃），通断式脉冲循环控 制（ON/OFF），最高炉温 1 000 ℃（板温 970 ℃）。这种炉子温度均匀，炉温波动可以小于 5 ℃， 钢板性能稳定均匀，表面质量好，自动化程度高。目前炉底辊一般采用 Cr25Ni35（Nb）材质，中空 不需要水冷，设有排气孔。炉底辊的壁厚和驱动电机功率决定处理钢板的厚度。炉底辊传动方式目 前多为单电机变频驱动，可实现灵活多变的控制。 在国际上，日本 NKK 京滨厚板厂辐射管加热辊底式炉设计处理的最大板厚为 200 mm，最大板宽 5 400 mm ，最大板长 26 mm；川崎水岛厚板厂辐射管式辊底炉长为 91.575 m ；新日铁君津厚板厂 辐射管式辊底炉最长达 96 m。其辐射管加热辊底式炉处理钢板无氧化、表面质量好、性能均匀稳定。 [1] 1 辊底式辐射管热处理炉的特点 11 第八届燃料炉委员会暨第