两相区淬火对5NiCrMo钢组织和性能的影响.pdfVIP

全国低台金钢、微台金非调质钢学术年会 i 两相区淬火对5NCrMo钢组织与性能的影响 沈俊昶，杨才福，张永权 (钢铁研究总院北京100081) 摘要t研究了两相区淬火+回火工艺(qq’T)对5NtCrMo钢力学性能的影响，采用光学显微镜和透射电 镜详细观察了微观组织结构，分析了组织演变规律及其对性能的影响。研究结果表明，5NiCrMo钢q。’T 处理后届强比降低。低温韧性提高．井改善了回火稳定性．板条状的回火=次马氏体+铁素体的混台组织 及回火过程中沿板条边界析出的逆转变奥氏体是试验钢获得嶷好性能的原因。 关键词：热处理；强度；韧性；届强比；逆转变奥氏体 TheEffectofIntercriticalThatmentonTheStructure and SteeI of5NiCrMo Properties Shen Junchang．YangCaifu，ZhangYongquan CentralIronandSteelResearch 100081，China Institute，Beijing Abstract：Themechanicalofan 5NiCrMosteel toa heat propertiesexperimental subjectedspecial treatment of consisting sequentialquenching(Q)，imeredticalquenching(Q’)andtempering(T) themicrostructural treatment were evolution Was measured，and QQ’T during systematically estimated transmissionelectron usingopticalmicroscope(oM)and microscope(TEM)．An treatmentfor andlow QQ’T regime toughnesscombination optimum strength temperatureimpact WaS a inthissteel achieved．Itisdemonstratedthatmicrostructureof subsequently consisting finelath—likemartensitewith andferrite asmall mainly hlightemperingstability impeachedby amountof austeniteWasobtainedin 5NiCrmo resultedin precipitated QQ’T-treatedsteel，which