焦炉炉墙陶瓷焊补技术的应用与实践 朱德伟 （鞍钢生产协力中心，鞍山 114021 ） 1 摘 要 为提高焦炉炉墙使用寿命、降低焦炉炉墙老化带来的炼焦生产过程中的超标排放，实现炉体工况稳 定，通过对焦炉炉墙陶瓷焊补技术所采用的焊补设备、焊补材料的性能、特点在炉墙实际维护维修作业中 的摸索与试验，使炉墙使用周期得到延长、炉墙严密性得到有效改善，为焦炉炉墙老化的维护维修提供了 宝贵的经验。 关键词 陶瓷焊补 焊接性能 焦炉寿命 Coke Oven Walls Ceramic Weld-repair Technology Application and Practice Zhu Dewei （Anshan Iron and Steel Company Production Together Center Ironmaking District,Anshan, 114021 ） Abstract To increase coke oven walls service life, reducing coke oven walls aging brings in the process of coking production, realizing the excess emissions by working stability of furnace, coke oven walls ceramic weld-repair technology adopted the weld-repair equipment, weld-repair material properties, characteristics in the furnace wall actual maintenance the homework attempts and test, making furnace wall use cycle get extended, and the furnace wall to effectively improve blurred for coke oven walls aging maintenance provided valuable experience. Key words ceramic weld-repair, welding performance, coke oven life 1 引言 焦炉陶瓷焊补技术是20 世纪70 年代发展起来的焦炉热修补技术，该技术具有焊补料性能好、焊补体寿 命长、设备安全性能好及对炉墙没有损害的特点。该技术在国外已得到广泛的应用，近年来，国内的一些大 中型企业逐步开始采用该技术进行焦炉维护维修。 2009 年鞍钢化工总厂在五炼焦1号～4 号焦炉开展了焦炉陶瓷焊补技术维修的试验，经过两年多的试验， 陶瓷焊补技术的优势和效果得到了充分的显现。长期制约焦炉生产的炉墙穿漏问题得到有效改善，有效解决 了炉墙穿漏带来的环保问题，同时大大减轻了焦炉日常维护的工作量，也延长了焦炉的使用寿命。 2 陶瓷焊补技术原理及特点 陶瓷焊补技术原理是使用一种由耐火材料和金属粉燃料组成的干混合物，使用特定的喷枪把这种混合物 喷射到要修理的区域。由于有氧气流输送，这种混合物通过 2000 ℃以上温度的放热反应在热修理表面持续 进行，因出现高温，待修补的砖表面迅速达到其熔化温度，使耐火材料与焊积上的材料非常紧密地结合在一 起。熔化的物质把小孔、接面、缝隙填满[4]。 朱德伟, 1967 年生,男,大学本科,工程师,从事焦化专业,鞍钢生产协力中心炼铁工区,联系电话邮箱：redseven@ 焦炉炉墙陶瓷焊补技术的应用与实践 8-331 陶瓷焊补的技术特点是它产生一个把焊接材料与耐火砖熔接在一起的非常紧密的接面。焊积在硅砖上的 耐火材