T4+镀锡板连续退火工艺模拟实验的研究.pdfVIP

T4 镀锡板连续退火工艺模拟实验研究 白会平 涂元强 柳长福 黄先球 郭玉华 （武钢研究院，武汉 430080 ） 摘 要 在实验室对镀锡板冷轧连续退火工艺进行了模拟实验，并通过金相显微镜、硬度和杯突分析，对试样连续 退火后的的性能进行了研究。综合实验结果，得出了 T4 （CA ）镀锡板的最佳退火工艺参数。实验结果表明在保温 时间相同的情况下，随着退火温度的升高，镀锡板晶粒相应长大，杯突值相应升高，而硬度值相应降低；在退火温 度不变的情况下，随着保温时间的增加，镀锡板晶粒增大。1 关键词 连续退火 模拟实验 T4 硬度 Simulated Experiment on Continuous Annealing Technique of T4 Tinplate Bai Huiping Tu Yuanqiang Liu Changfu Huang Xianqiu Guo Yuhua （Research and development Center of WISCO, Wuhan, 430080 ） Abstract The simulated experiments of continuous annealing technique in the cold reduced process of tinplates were studied in the lab. By metallographic microscopy, rockwell hardness test and cupping test, the properties of tinplates after continuous annealing were further determined in this paper. The optimal continuous annealing parameter for T4 tinplate was obtained from the simulated experiments. The results also show that the crystal sizes and the cupping values increase while the hardness values decrease accordingly with the increase of continuous annealing temperature under the same holding time and that the crystal sizes increase with the increase of holding time under the same annealing temperature. Key words continuous annealing, simulated experiment, T4, hardness 电镀锡板是两面镀有纯锡的冷轧低碳薄钢板或钢带，它将钢的强度和成型性同锡的耐蚀性、可焊性和美 观结合于一种材料之中[1, 2] 。 处理镀锡原板的退火方式有连续退火（CA ）和罩式退火（BA ）两种。连续退火的镀锡板原板同罩式退 火相比[3]，优点有力学性能均匀、板形良好、耐蚀性良好；缺点是由于加热和冷却都很快，所以不能得到适 合于深冲加工用的较软的镀锡原板。 本文通过实验室对连续退火生产工艺进行了模拟试验，重点研究了生产 T4 硬度级别镀锡板连续退火工 艺参数。 1 实验方法 实验材料为武钢冷轧厂 HC 轧机轧制的冷轧钢板，板厚为 0.20mm 。冷轧钢板的主要化学成分 （mass% ）： 0.032 C，0.014 Si，0.340 Mn，0.009 P，0.009 S，0.029 Als，0.003 N 。 采用日本真空理工株式社的