直流负载条件下Cu-Cr-Zr-Ag合金的电侵蚀特性.pdfVIP

2014年5月 贵 金 属 M ay2014 第 35卷第2期 PreciousMetals Vo1．35，No．2 ElectricalErosionCharacteristicsofCu--Cr-Zr-AgAlloy ContactunderDC Load WANG Song，CHENYongtai，ZHANGJiming，WAN GSaibei，LIU M anmen，YANGYunfeng，XIEM ing (StateKeyLaboratoryofAdvancedTechnologiesforComprehensiveUtilizationofPlatinumMetals， KunmingInstituteofPreciousMetals，Kunming650106，China) Abstract：TheanalysisofelectricalerosioncharacteristicsofcontactsunderDC loadisconducivetothe in—depthstudyoftheelectricalerosionmechanism．Theelectricalexperimentsontheelectricalerosion statusoftheCu—Cr-Zr-AgalloycontactsunderDC loadof25V／15A andtheelectricalerosionmechanism were carried outby electricalcontacttestmachine and SEM ．The surface micromorphologies． microstructuresandmaterialtransferphenomenonofthecontactswerestudiedin thisPaDeLTheresults showed thattheCu．Cr-Zr-Ag contactshaveexcellentanti—weldingproperties．Theelectricalerosion surfacesofthematerialshoweda1argenumberofpaste—likecoagulum andbubbles．Therearesome micro．cracksexistingon thesurfaceoftheCu—Cr=Zr—Agalloycontacts．Theobviousmaterialtrna sfer phenomenonoccursbetweenthemovableandstaticcontactsunderDCload． Keywords：metalmaterial；Cu—Cr-Zr-Agalloy；DC load；electricalerosion；microtophography CIFnumber：TG146．32 Documentcode：A ArticleID：1004．0676(2014)02—0001—05 直流负载条件下Cu-Cr-Zr-Ag合金的电侵蚀特性 王 松，陈永泰，张吉明，王塞北，刘满门，杨云峰，谢 明 (昆明贵金属研究所 稀贵金属综合利用新技术国家重点实验室，昆明 650106) 摘 要：直流负载下触头的电侵蚀特性分析有助于深入研究其电弧侵蚀机理。通过对 Cu—Cr-Zr-Ag 合金触头进行电性能实验，研究了25V／15A直流负载条件下，合金触头的电侵蚀情况。采用电接 触试验机和扫描电镜，研究了合金材料的电弧侵蚀机理，表面形貌，微观结构和材料转移现象。结 果表明：Cu-Cr-Zr-Ag合金触头具有优异的抗熔焊性能，合金触头的电弧侵蚀微观形貌表现为浆糊 状凝固物和气泡，且在触头侵蚀表面存在微裂纹。直流负载条件下动静触头间会发生明显的材料转 移现象。 关键词：金属材料