热处理对铁基纳米晶薄带高频磁导率的影响.pdfVIP

工艺·技术·应用 热处理对铁基纳米晶薄带高频磁导率的影响 李 青，李 博，赵伟伟 （太原钢铁集团电气设备修造有限公司，山西太原 030000 ） 摘 要：利用单辊快淬法制备 FeCuNbSiB 铁基纳米晶薄带。分析了热处理温度、热处理时间及冷却条件包 括冷却速度与氧化程度对 FeCuNbSiB 铁基纳米晶薄带高频磁导率的影响。随热处理温度的上升，铁基纳米晶铁 芯的磁导率先增大而后出现不同程度的降低；在一定热处理温度，随热处理时间的延长，铁基纳米晶铁芯的磁 导率逐渐减小；较快的冷却速度与氧化会降低铁基纳米晶铁芯的高频磁性能。 关键词：铁基纳米晶合金；热处理；磁导率 中图分类号：TM275 文献标识码：A 文章编号：1001-3830(2015)03-0051-03 Influence of heat-treatment on the high-frequency permeability of Fe-based nano-crystalline ribbon LI Qing, LI Bo, ZHAO Wei-wei Electrical Equipment Repair Manufacture Co, Ltd, Taiyuan Iron and Steel Group, Taiyuan 030000, China Abstract: FeCuNbSiB Fe-based nano-crystalline ribbon was prepared by single-roller rapid quenching technology. The influence of heat-treatment temperature and time and cooling conditions including cooling rate and oxidation on high-frequency permeability of FeCuNbSiB nanocrystalline ribbon, and the way to get the maximum high-frequency permeability were investigated. As the heat-treatment temperature increases, the permeability of Fe-based nanocrystalline cores increases first and then decreases to varying degrees. Under a certain temperature, as the heat-treatment time extends, the permeability decreases gradually. Fast cooling rate and oxidation lowers the high-frequency magnetic performance of Fe-based nanocrystalline cores. Key words: Fe-based nanocrystalline ribbon ； heat-treatment ； permeability 电路混合工作时会产生大量高频电磁干扰，不仅降 1 引言 低了电源质量，而且影响其他设备的正常工作。因 FeCuNbSiB 铁基纳米晶合金是在铁基非晶合 此在开关电源中，广泛使用着各种起贮能和滤波作 金中加入微量的 Cu 和 Nb ，再经过