由Fe基金属玻璃制备的注塑软磁体.pdfVIP

工艺·技术·应用 由Fe 基金属玻璃制备的注塑软磁体 耿保山 （上海葆硕磁性材料有限公司，上海 201800 ） 摘 要：以Fe 基金属玻璃软磁粉末为原料，通过常规的钕铁硼粘结磁体注塑工艺，制备了尼龙基的软磁注 塑磁体，注塑磁体中尼龙质量分数为 15%。对材料的表面形貌、力学性能和磁性能进行了表征。实验结果显示， 传统尼龙注塑粘结磁体工艺可以用于制备金属玻璃注塑软磁体，其力学和机械性能与传统钕铁硼注塑磁体相当， 并且具有金属玻璃的优良软磁性。 关键词：注塑成型；金属玻璃；软磁材料 中图分类号：TM274 文献标识码：A 文章编号：1001-3830(2015)03-0065-03 Nylon injection molded soft magnetic material prepared from Fe-based metallic glass GENG Bao-shan Shanghai Baoshuo Magnets Co, Ltd, Shanghai 201800, China Abstract: Fe-based metallic glass powder was utilized to prepare injection molded paramagnets with 15wt% Nylon resins via conventional injection method. The surface morphology, mechanical and magnetic properties of the material were characterized. The result shows that injection modeled paramagnets can be prepared using conventional injection molding for bonded magnet, with comparable mechanic and surface morphological feature to the normal injection molded NdFeB magnet, implying that the method is practical, and the product exhibits excellentsoft magnetic performance. Key words: injection molding; metallic glass; soft magnetic material 金属玻璃又称非晶态合金，是通过热力学手 1 引言 段，将金属元素在熔点之下保持非晶型的无定形 注塑成型磁性材料是科研与工业中广泛应用 态，其结构与无机玻璃类似。自从上世纪 50 年代 的一种材料。注塑磁性材料结合了高分子材料加工 由过冷法制备出来后，得到了领域内密切的关注和 的优势和特点，一般是将高分子材料（如尼龙等） 发展，它结合了金属和玻璃的优点，具有强度高、 作为粘结剂和磁粉（如铁氧体、NdFeB 磁粉等）有 硬度高、一定的韧性和刚性等显著优势[3,4] 。在金 效均匀混合后，采用熔融注射方法一次成型，与一 属玻璃基础上，由铁基等磁性金属元素制备的玻璃 般金属磁性材料相比，粘结磁性材料成型工艺简