硅钢边部缺口在冷轧过程中延展行为研究.pdfVIP

硅钢边部缺口在冷轧过程中的延展行为研究 闫玉曦 陈建钧 潘红良1 （华东理工大学机械与动力工程学院，上海 200237 ） 摘 要 针对硅钢边部缺口在轧制过程中的扩展现象进行了实验研究，发现 I 形缺口在连续不可逆轧制后扩展成V 形缺口；而对于 U 形缺口，当缺口长度小于宽度时，轧制后缺口有被“碾”平的趋势，甚至最终消失；缺口的长 宽比越大，缺口扩展开裂的趋势越明显，且缺口扩展的趋势随着压下量的增大而增强。另外，钢板的硅含量越高材 料的韧性越差，越容易形成边裂。 关键词 冷轧 硅钢 边部缺口 压下量 Study on Extending Behavior of Edge Notches of Silicon Steel Strips during Cold Rolling Process Yan Yuxi Chen Jianjun Pan Hongliang (East China University of Science and Technology, Shanghai, 200237) Abstract An experimental investigation of the extending behavior of edge notches of silicon steel strips during cold rolling process is undertaken in the present study. Experiment results showed that I type openings expanded into V type ones in rolling process; for U-shaped gaps, when the length of the notch is less than width, the gaps had the tendency to disappear; with the increasing of the aspect ratio and the reduction, the tendency of the expansion becomes more and more obvious; the higher the content of the silicon is, the easier edge crack will occur. Key words cold rolling, silicon steel, edge crack, reduction 1 引言 冷轧硅钢板在进入冷轧机组前要经历酸洗、剪边等一系列前序操作，会在薄板边部留下各类微小缺陷， 进入轧制区时这些缺陷将快速扩展，最终导致带钢边部形成宏观裂口，严重的还会导致断带事故，降低产品 成材率，造成严重的经济损失[1] 。因此，如何减少冷轧过程中边裂事故的发生已经成为冷轧生产中迫切需要 解决的问题。 目前对轧制边裂形成机理的认识还不成熟，现有的研究主要集中在热轧边裂的成因和防护措施上。Han[2] [3，4] 等研究了热轧硅钢边裂的原因及防护方法，卢凤喜 介绍了新日铁和川崎公司在热轧硅钢边裂防护方面的 [5] [6] 措施，葛建新 等分析了热轧带钢边裂的成因，陈伟 等运用金相显微镜、扫描电镜等手段研究了碳钢板在 热轧过程中的边裂原因，这些文献的研究结果显示冶炼脱氧不良、钢中夹杂物和有害杂质以及轧制过程中的 温度分布不均是造成热轧边裂的主要原因。目前针对冷轧边裂成因和机理的研究相对较少。 边裂由初始缺陷连续扩展而来，在生产实际中，边裂现象被发现时已经是在连轧出口处，此时的缺口已 经经历了多道次的轧制，而在生产实际中无法观察到每一道次轧制对缺口扩展的影响。因此，分析边部缺口 闫玉曦，男，博士，从事冷轧带钢断带及边裂研究，yyx_2116@163.com 第八届（2011 ）中国钢