CFHI TECHNOLOGY 10.3969/j.issn.1673-3355.2011.02.010 马氏体钢中啄-铁素体的表征及影响 赵美兰1 摘要：利用冲击试验机、维氏硬度计、金相显微镜、扫描电镜和能谱分析技术研究工业生产大型锻件马氏体耐热 钢中的啄-铁素体含量以及啄-铁素体对冲击性能的影响。研究表明：啄-铁素体是一种富W 、Mo、Cr 和V 且贫Mn 相，接近水口端比冒口端含量高，它的存在是造成马氏体耐热钢冲击韧性低的主要原因。可通过控制铁素体形成 元素到最低限和奥氏体形成元素到最高限，抑制啄-铁素体的析出，获得完全马氏体组织及良好的综合力学性能。 关键词：马氏体耐热钢；啄-铁素体；Creq ；冲击性能 中图分类号：TG115 文献标识码：B 文章编号：1673-3355 （2011）02-0010-05 Characteristics of -Ferrite and Its Effect on Impact Property in Martensitic Heat Resistant Steel Zhao Meilan Abstract: Although such steel normally have a fully martensitic microstructure, they are susceptible to the formation of 啄- ferrite. 啄-ferrite and its effect on impact property in large -scale martensitic heat resistant steel were researched via impact test, Vickers hardness test, optical microscope, SEM and EDS. The results indicated that, 啄-ferrite was W, Mo, Cr and V- enriched but poor -Mn phase, and there was more 啄 -ferrite in water slot than that in feeder head. Its existence led to extremely low impact toughness. A fully martensitic microstructure and excellent general mechanical property could be achieved through controlling the austenitic-formation elements to lower limit and ferrite-formation elements to upper limit. Key words: martensitic heat resistant steel; 啄-ferrite; Cr equivalent; impact toughness 新型9%~12%Cr 马氏体钢是超临界电站机组 则认为，只有当其超过 1%时才会具有较大的影响， 中应用最多的一类材料，被广泛应用于锅炉和汽轮 否则几乎不产生影响，甚至可以略微提高冲击韧 机的许多部件，包括锅炉管、连箱、管道、汽缸、 性。以上研究工作 限于实验室用小型钢锭，而针 [ 1~2] 叶片和转子等 。为了保证火电机组在长期服役 对工业生产大型锻件马氏体耐热钢中啄-铁素体的 过程中的安全，除对材料低周疲劳性能、蠕变强度 表征及其对冲击性能影响的研究还未见报道。 和应力腐蚀敏感性等有严格要求外，对冲击韧性也