用于高强度聚焦超声热消融的PAA模块：模块的制作及声学参数的测量.pdfVIP

维普资讯 第25卷第6期 声 学 技 术 Vo1．25，No．6 2006年 12月 TechnicalAcoustics Dec．，2006 PAA phantom foruseinthermalablationofhigh intensityfocusedultrasound：Phantom fabrication andacousticparametersmeasurements HU Bing，JIANG Li—xin，HUANG Ying (DepartmentofUltrasoundinMedwine，ShanghaiJiaotongUniversityAffiliatedSixth PeopleSHospital。Shnaghai200233，China) Abstract： Objective Anopticallytransparentphantom usedforthermalablationofHIFUhas been developed with acoustic parametersmeasured． Methods Thecolorand transparency of differentconcentration phantomswereobserved．Propertiesincludingdensity，acoustic speed and acousticattenuationofPAA gelphantom weremeasured． Results (1)PAA gelphantom was amberand transparent．The colorbecame heavierand transparency decreased with theegg—white concentrationincreasing．(2)ThedensityofPAAgelphantomwassimilartowater，whichwasfrom 1．0250g／cm to 1．0617g／cm ．Therewasasignificantcorrelationbetween sound speedandphantom concentration．Ihe acoustic attenuation was from 0．125dB／cm to 0．329dB／cm，increased with the phnatom density nad transducer frequency increasing． Conclusions PAA gelphantom was homogeneousandagoodmimickingphantom ofrHIFU thermalablation．Theexperimentresultshad asatisfiedreproducibility． Keywords： polyacrylamide(PAA)；phantom；highintensityfocusedultrasound (HIFU)；therma ablation；acousticpraameters 用于高强度聚焦超声热消融的PAA模块 模块的制作及声学参数的测量 胡 兵，姜立新，黄 瑛 (上海交通大学附属第六人民医院超声医学科，上海 200233) 摘要： 目的 研制一种透明的用于高强度聚焦超声热消融的PAA模块，并对其声学参数进行测量。 方法 观察 模块浓度的不同所致颜色与透明度