特殊钢筋溷凝土组合梁的疲劳性能.pdfVIP

J. Cent. South Univ. Technol. (2010) 17: 142−149 DOI: 10.1007/s11771−010−0023−5 Fatigue properties of special kind of reinforced concrete composite beams HU Tie-ming(胡铁明)1, 2 1 1 , HUANG Cheng-kui(黄承逵) , CHEN Xiao-feng(陈小锋) 1. State Key Laboratory of Coastal and Offshore Engineering, Dalian University of Technology, Dalian 116024, China; 2. School of Architectural and Civil Engineering, Shenyang University, Shenyang 110044, China © Central South University Press and Springer-Verlag Berlin Heidelberg 2010 Abstract: The special reinforced concrete composite beam consists of a steel fiber reinforced self-stressing concrete composite layer and a reinforced concrete T-beam, and constructional bars are set up at their bonding interface. Fatigue properties of the composite beam under the action of negative moment were experimentally studied. Through inverted loading mode the load-bearing state of a composite beam was simulated under the action of negative moment. With the ratios of constructional bars being 0, 0.082% and 0.164% respectively as parameters, the effects of constructional bars on the properties of composite beam, such as fatigue life, crack propagation, rigidity loss as well as damage behavior of bonding interface, were studied. The mechanism of the constructional bars on the fatigue properties of the composite beams and the restriction mechanism of crack widths and rigidity loss were analyzed. The test results show that the constructional bars can enhance the shear resistance of the bonding interface between composite layer and old concrete beam and restrict expanding of steel fiber reinforced self-stressing concrete, which are beneficial to synergistic action