ADI CADI 在冶金矿山等行业中的应用及发展前景 1 2 1 3 3 3 金海 叶学贤 李国禄 张会友 边泊乾 王绍勤 1.河北工业大学材料科学与工程学院;2.湖北汽车高科技投资公司;3.迁西奥蒂爱机械铸 造有限公司） 摘要：本文论述了ADI 和CADI 的耐磨性能特点，以及在磨球、衬板、锤头等冶金矿山配件 中的应用现状，另外，讨论了ADI 和CADI 的应用发展前景。 关键词：球墨铸铁;等温淬火;碳化物;耐磨性;冶金矿山 Application and Developing Prospect of ADI and CADI in Metallurgical and Mining Area 1 2 1 3 3 3 (Liu-Jin-hai ,Ye-Xue-xian ,Li-Guo-lu ,Zhang-Hui-you ,Bian-Bo-qian ,Wang-Shao-qin ) ( 1.School of Materials Science and Technology Hebei University of technology; 2.Hubei Automobile Gaoke Investment Corporation ; 3.Qianxi ADI Machinery Casing Corporation) Abstract:This paper mainly dealt with the abrasive resistance of ADI and CADI, and the application in repairing pieces of metallurgical and mining area, such as mining ball, lining board , hammer and so on. In addition, the developing prospect of ADI and CADI was also discussed. Key Words: Nodular cast iron ,Austempering,Carbides,Abrasive resistance,Metallurgy and mining 1 前言 铁矿石是炼铁、炼钢的主要原料，在铁矿石生产过程中，都必须经过采掘、破碎、研磨 和选取等工艺程序。在这些工艺过程中，机器设备和零部件都会因磨损而必须更 。表 1 为在冶金矿山工业中主要的消耗工序及其典型易损件。 表1 冶金矿山工业中主要的消耗工序及其典型易损件[1] 消耗工序 钻孔 采掘 破碎 研磨 排尾矿 主要 潜孔钻头、牙 挖掘机斗齿、 圆锥破碎机 衬板 杂浆泵壳体、 磨损零件 轮钻头 履带板 破碎壁、齿板 磨球 叶轮、护套 耐磨材料在冶金矿山等工业领域整个能量和经济成本的消耗中占有相当大的比例。据国 [2] 内不完全统计 ，仅破碎设备及采掘机斗齿、渣浆泵等损失，每年不少于 70 亿，其中，磨 球不少于40 亿，衬板15 亿，锤头8 亿，斗齿5 亿。美国每年的磨损损失近1200 亿美元， 约占国民经济的4%，其中，磨料磨损占总损失的 1/2 ，德国每年磨损损失约500 亿马克。 [3、4] 按照材料消耗讲，国内每年消耗金属耐磨材料约达300 万吨以上 ，其中，磨球消耗近180 万吨，而冶金矿山消耗的磨球占磨球消耗总量的70 ﹪；球磨机和各种破碎机衬板消耗近30 万吨，轧辊消耗近50 万吨，各种工程挖掘机和装载机斗齿、各种耐磨输送管道、各种破碎 机锤头和鄂板、各种履带板消耗也超过50 万吨。 此可见，如何提高冶金、矿山等工业领 域的易损件使用寿命，降低生产成本，一直是国内外研究和生产企业所重视的