原位合成TiC增强420不锈钢的力学性能和抗磨损性能.pdf

Journal of Southeast University (English Edition) Vol. 20 No. 4 Dec. 2004 ISSN 1003 Tensile and wear properties of TiC reinforced 420 stainless steel fabricated by in situ synthesis Wang Li Sun Yangshan Fan Ouan Xue Feng Duan Zhichao (Department of Materials Science and Engineering, Southeast University, Nanj ing 2, CChhiinnaa)) 009966,, CChhiinnaa)) Abstract: TiC particle reinforced 420 stainless steel matrix composites Were fabricated, and the microstructure, tensile properties and Wear resistance of the composites Were studied. The experimental results indicate that the distribution of TiC particles With size of 5 to 10 !m in diameter is uniform if the volume fraction of TiC is loWer than 6% . HoWever, slight agglomeration can be observed When the TiC content exceeds 6% . With the increase of TiC content the tensile and yield strength of the composites prepared increases and reaches the maximum When the volume fraction of TiC increases to 5% . Further increase of TiC content causes reductions of yield and tensile strength . The ductility of the composites shoWs a monotone decrease With the increase of TiC addition . The introduction of TiC into 420 stainless steel results in significant improvement on Wear resistance, Which reaches a steady level When the volume fraction of TiC increases to 11% and does not shoW oobbvviioo