Trans. Nonferrous Met. Soc. China 24(2014) 2574−2580 Microwave absorption properties of FeSiBNbCu glass-covered amorphous wires Xiao-dong WANG1 2 3 1 1 1 , Jing-shun LIU , Fa-xiang QIN , Huan WANG , Da-wei XING , Jian-fei SUN 1. School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China; 2. School of Materials Science and Engineering, Inner Mongolia University of Technology, Hohhot 010051, China; 3. 1D Nanomaterials Group, National Institute for Materials Science, 1-2-1 Sengen, Tsukuba, Ibaraki 305-0047, Japan Received 27 August 2013; accepted 28 April 2014 Abstract: Coaxially dielectric samples consisting of different packing ratios of glass-covered Fe Si B Nb Cu amorphous wires 73.5 13.5 9 3 1 embedded in a paraffin wax matrix were fabricated, and the influence of short-wire packing ratio (3%−9% in mass fraction) and thickness (1−7 mm) on the microwave absorption properties was systematically investigated in microwave frequency range of 2−18 GHz. X-ray diffraction (XRD), differential scanning calorimetry (DSC), scanning electron microscopy (SEM) and scalar network analyzer (SNA) were used for characterizing microstructure and evaluating microwave absorption properties. Experimental results show the significant frequency (6−18 GHz) dependence of the complex relative permeability and permittivity. The reflection loss (RL) with different thickness and short-wire packing ratio reveals that the composite sample containing 7%