耐铝及其合金熔体腐蚀磨损材料的研究进展.pdfVIP

Trans. Nonferrous Met. Soc. China 25(2015) 1715−1731 Review on corrosion-wear resistance performance of materials in molten aluminum and its alloys Xian-man ZHANG, Wei-ping CHEN Guangdong Key Laboratory for Advanced Metallic Materials Processing, South China University of Technology, Guangzhou 510640, China Received 5 August 2014; accepted 28 December 2014 Abstract: The failure caused by the corrosion-wear of molten aluminum and its alloys is one of the main problems in aluminum industry. In this work, the resistance behavior of various materials, including Fe-based alloys, ceramics and corresponding high apparatus of corrosion-wear in molten aluminum and its alloys, were reviewed. The synergistic effect of corrosion and wear was discussed based on corrosion and wear mechanics. The effects of dynamic agitation due to rotating of friction pairs, physical property of liquid metal and size of grain etc., on the corrosion-wear resistance performance were investigated. In addition, the characteristics of corrosion-wear resistance performance of materials in molten aluminum and its alloy were summarized. According to our recent progress referred to kinds of materials, especially a TiAl /Ti AlC /Al O composite, the ceramics/metal composites with a 3 3 2 2 3 co-continuous structure will be of great advantage in the field of corrosion-wear environment of molten aluminum and its alloys. Key words: molten aluminum; aluminum alloy; corrosion; wear; synergistic effect; intermetallics industry, s