新型炭材料990105 新型炭材料 NEW CARBON MATERIALS 1999年 第14卷 第1期 Vol.14 No.1 1999 短切炭纤维表面改性 及其增强聚四氟乙烯复合材料性能的研究 施　凯 摘　要　采用偶联剂对短切炭纤维表面改性，然后和聚四氟乙烯(PTFE)粉料混合，冷 压成型，烧结固化等手续制备了短切炭纤维增强PTFE复合材料。研究了不同类型偶联 剂，其最佳用量和表面改性的工艺条件。结果表明，复合材料的力学性能和耐化学腐 蚀性能均优于同类材料。 关键词　短切炭纤维　表面改性　偶联剂　树脂基复合材料　聚四氟乙烯 分类号　TB 332 RESEARCH ON THE MODIFICATION OF CHOPPED CARBON FIBRE AND PREPARATION OF CF REINFORCED PTFE COMPOSITE Shi　Kai (Taiyuan university of technology,Taiyuan 030024) ABSTRACT　The chopped carbon fiber surface was modified by coupling agent,and then the polytetrafluoroethylene(PTFE)-based composite reinforced by thus modified CF was prepared via PTFE powder mixing with chopped CF,cold moulding and green mould sintering,ect.The effects of different types coupling agents,their relative contents and the technological conditions of CF surface modification on resultant composite properties were studied.Results show,the mechanical properties and resistance aggainst chemical corrosion of prepared in this study composite were preferable to those of other same-class materials. KEY WORDS　Chopped carbon fibre ，Surface modification,Coupling agent， Polytetrafluoroethylene composite 　　炭纤维自六十年代开发成功以来，由于其优异的力学性能和不可代替的某些特性 而得到了突飞猛进的发展，它被广泛应用于要求轻质、高弹性模量，高强度和耐腐蚀 的特殊领域。炭纤维一般不单独使用，而是和树脂及其它基体材料制成复合材料。在 树脂基复合材料中采用环氧树脂为基体时，可有效地提高其比刚度；采用酚醛树脂和 ［1］ 聚酰亚胺为基体时，则主要是考虑其耐热稳定性和耐烧蚀性 ；最近几年又相继对 聚酰胺，聚碳酸脂等基体的复合材料进行了研究。聚四氟乙烯（PTEF）树脂以耐腐 蚀、耐磨、耐热、电绝缘性和自润滑性等箸称，若用短切炭纤维增强制成复合材料， 新型炭材料990105 密度仅为钢材的四分之一，而强度、弹性模量、摩擦系数、耐化学腐蚀性等均远远好 于钢材，也优于其它复合材料。然而，这方面近几年来开发研究甚少，究其原因主要 是找不到一种适宜的成型方法，另外所得材料的力学性能也不很高。 ［2］ 　　近期研究表明 ，短切炭纤维在增强聚四氟乙烯时，由于炭纤维表面过于光 滑