低温等离子体表面改性高分子材料研究进展(论文资料).pdfVIP

86 综述 专论 , , (, 330063) [ ] 综述了低温等离子体技术的最新进展, 指出目前最具开发潜力的低温等离子体有大气压下辉 放电等离子体和介 质阻挡放电等离子体经低温等离子体处理的高分子材料表面发生多种物理和化学变化, 例如产生刻蚀形成致密的交联层以及引 入极性基团, 使材料的亲水性粘结性生物相容性等得到改善, 故低温等离子体处理技术广泛用于高分子材料的表面改性, 重点介 绍了低温等离子体在医用高分子材料合成纤维材料薄膜材料中的研究概况和进展 [ ] 低温等离子体; 高分子材料; 表面改性 [ ] TQ 316. 6 [] A [] 1001- 3660( 2009) 05- 0086- 04 Research Progress of the SurfaceM odification of Polym er M aterialsM odified by Low Temperature Plasma MENG J iang y an, LI Weid ong, WAN G Yuny ing ( College ofM aterial Sc ience and Eng ineering, Nanchang H angkong Un iver ity, N anchang 330063, Ch ina) [Abstract] The new e t progre of low tem perature pla m a techn ique w a rev iew ed and that the m o t poten tial developm ent of low tem perature pla m a w a ind icated including the glow d i charge pla m a at atm o pheric pre ure and the dielectric barrier di charge ( DBD ) pla m a. The polym er m aterial urface treated by low temperature pla m a took place a lot of phy ical and chem ical change , uch a etch ing, form ing a den e layer of cro link ing, a w ell a the in troduction of polar group , o that th i m aterial hydroph ilic, adhe ive, biocom patibility w ere mi proved. For tho e rea on , the low tem perature pla m a are w idely u ed in urface m od if ication of the polym er m aterial. The application and developm ent of low tem perature p lam a in the urfacem od if ication ofm edical polym er m aterial, ynthe i fiber m ater i al and film m aterial m o tly w ere in troduced. [Key words] Low tem perature p lam a; Polym er m aterial; Surface modification 0 , , , , ,