HBP-NH2改性棉纤维吸附剂的制备及性能研究.pdf

Test and Standard 标准与测试 HBP-NH 改性棉纤维吸附剂的制备及性能研究 2 文｜孙 凤 臧传峰 闫 腾 张德锁 陈宇岳 林 红 摘要：本研究通过氧化活化棉纤维的方法将端氨基超支化聚合物（HBP-NH2 ）接枝到棉纤维表面，成功制 备了一种HBP-NH2 改性棉纤维吸附剂，并以Cd2+ 的吸附量为依据对吸附剂的制备工艺进行了优化。研究表 明HBP-NH 改性棉纤维吸附剂最佳制备工艺为：在60 ℃下，pH值为11.03的20 g/L HBP-NH 溶液中（浴比 2 2 1 ∶50 ），接枝反应 2 h ，所制备的改性棉纤维对Cd2+ 的吸附量最高，可达38.94 mg/g 。 关键词：棉纤维；接枝；端氨基超支化聚合物；镉离子 中图分类号：TQ085 文献标志码：A Preparation of Adsorbent Based on Modification of Cotton Fibers by HBP-NH2 and Its Property Abstract: A modified cotton fiber adsorbent was prepared successfully by grafting amino-terminated hyperbranched polymer (HBP-NH ) onto oxidized cotton fibers. Its technology of preparation was optimized 2 based on the adsorption quantity of Cd2+ . The results showed that the modified cotton fibers have the highest adsorption capacity up to Cd2+ when 20 g/L HBP-NH reacted with oxidized cotton fibers at 60 and 11.03 2 ℃ pH value for 2 h. The adsorption quantity of Cd2+ could reach 38.94 mg/g. Key words: cotton fiber; grafting; HBP-NH ; Cd2+ 2 镉是一种毒性很强的重金属，极微量的镉就可对人体 有丰富的氨基和亚氨基，可以用于重金属的吸附。 造成伤害。它具有稳定、积累和不易消除的特点，通过食物 本文利用HBP-NH2接枝到氧化棉纤维表面，制得HBP- 链富集，可使人体产生慢性中毒，甚至使人疼痛而死。1993 NH2改性棉纤维吸附剂，并对制备的吸附剂进行了表征。同 年世界肿瘤研究机构（IARC ）将镉定义为人类第IA致癌 时，以对Cd2+ 的吸附量为参照，探讨了HBP-NH 浓度、接枝 2 物。因此，含镉废水的有效处理刻不容缓，研究开发高效、