纳米ZnS/SiO2/Fe3O4结构的合成及其光 致发光效应的探究 唐健 P 张平P奚政 P陈杰 P钟浩 PPreparation of Core-shell Fe3O4/SiO2/ZnS Nanoparticles and Optical Characterization Research 摘要： 本实验制作了Fe3O4/SiO2/ZnS三壳层结构，并对其特殊的荧光性质做了检测。应用内衬Teflon反应釜制备纳米Fe3O4粒子，运用Stober方法在其表面包裹SiO2,最后运用水浴法将ZnS包裹在其最外层。实现了用较简单的方法制备集荧光磁场双重效应于一体的纳米粒子。并对其光致发光效应做了相应的研究与讨论。 关键词：光致发光，磁性，ZnS，纳米粒子，核壳结构 In this article, we report a facile way in synthesizing the three-shell Fe3O4/SiO2/ZnS structure, and its fluorescent property is measured and discussed. In our experiment, we first obtain the nano-particle Fe3O4 with the high-temperature pot, then Stober way is used to enclose Fe3O4 with SiO2; finally, using hydrothermal method, we strived to coat the SiO2-enclosed- Fe3O4 particle with ZnS, which shows certain fluorescent property. Furthermore, when exterior magnetism is applied, the fluorescent phenomenon becomes more interesting and more complicated. As the last part, we give some investigation and discussion concerning the magnetism-related photoluminescence of the nano-particle that we have prepared. Keywords: fluorescent; magnetism; sulfur zinc; nano-particle; core-shell structure； 一.引言 纳米材料研究是目前材料科学中的一个热点，因其具有独特的表面效应，体积效应以及量子尺寸效应而产生特殊的理化特性相应发展起来的纳米技术被公认为时21世纪最具有前途的科研领域之一。II-IV组化合物ZnS作为一种直接宽带系（3.66V)的半导体材料及一种重要的发光材料，在化工、电子、生物医学等诸多领域都有广泛的应用。近年来，将ZnS的发光效应，Fe3O4纳米粒子的超顺磁效应有效地结合起来的ZnS/Fe3O4纳米粒子已越来越多的被制备出来。2009年，复旦大学的材料科学与功能材料实验室中发现了一种用以合成Fe3O4/ZnS包覆纳米粒子的新方法，叫做corrosion-aided Ostwald rirening。在一个外磁场的作用下，包覆纳米粒子仅需几分钟的时间就可以在磁场附近发生聚合，表现了其良好的磁性，如图2所示。在激发光的照射下，这种团聚物可以发出蓝色的荧光长达18分钟，显示了其显著的荧光效应.(图1，图2，图3）[1] 图1 图2 图3 北京大学的微结构与先进功能材料研究所同样制备出了Fe3O4/ZnS包覆纳米粒子，图4左图显示了Fe3O4的形貌，可见它的结构并不紧凑，仍会出现孔洞。右图说明ZnS已经成功包覆，空洞已经消失了，而且结构也是更加完整与紧凑。图5显示的是荧光效果。在紫外光的激发下，包覆纳米粒子的发光强度（右边）要比为包覆的纯的Fe3O4的发光强度要明显，这为生物观测提供了可能。图6是Fe3O4与包覆纳米粒子的对磁场感应的比较。从图中可见包覆纳米粒子的感应速度会更快一些，这显示了它良好的磁性。[2] 图4 图5