《金刚石混杂碳化硅铝复合材料的组织与热物理性能（英文版）》.pdfVIP

Trans. Nonferrous Met. Soc. China 25(2015) 170−174 Microstructure and thermophysical properties of SiC/Al composites mixed with diamond 1,2 1 1 2 1 Hong GUO , Yuan-yuan HAN , Xi-min ZHANG , Cheng-chang JIA , Jun XU 1. National Engineering Technology Research Center for Nonferrous Metals Composites, Beijing General Research Institute for Nonferrous Metals, Beijing 100088, China; 2. School of Materials and Engineering, University of Science and Technology Beijing, Beijing 100083, China Received 8 January 2014; accepted 5 March 2014 Abstract: The thermophysical properties of the SiC/Al composites mixed with diamond (SiC-Dia/Al) were studied through theoretical calculation and experiments. The thermal conductivity and the thermal expansion coefficient of the SiC-Dia/Al were calculated by differential effective medium (DEM) theoretical model and extended Turner model, respectively. The microstructure of the SiC-Dia/Al shows that the combination between SiC particles and Al is close, while that between diamond particles and Al is not close. The experimental results of the thermophysical properties of the SiC-Dia/Al are consistent with the calculated ones. The calculation results show that when the volume ratio of the diamond particles to the SiC particles is 3:7, the thermal conductivity and the thermal expansion coefficient can be improved by 39% and 30% compared to SiC/Al composites, respectively. In other words, by adding a small amount of diamond particles, the thermophysical properties of the composites can be imp