* Observation of Gamma Irradiation-Induced Suppression of Reverse Annealing in Neutron Irradiated MCZ Si Detectors Zheng Li1, Rubi Gul1, Jaakko Harkonen2, Martin Hoeferkamp3, Jim Kierstead1, Jessica Metcalfe3, and Sally Seidel3 1Brookhaven National Laboratory, Upton, NY 11973, USA 2Helsinki Institute of Physics, Finland 3University of New Mexico, NM, USA 12th RD50 - Workshop on?Radiation hard semiconductor devices?for very high luminosity colliders Ljubljana, Slovenia, 2-4 June 2008 *This research was supported by the U.S. Department of Energy: Contract No. DE-AC02 -98CH10886 Outline 1. Motivation of mixed radiations 2. Experimental Overview: samples, radiations and measurements 3. Experimental results of TCT current pulse shapes on samples after 1 MeV neutron irradiation 4. Experimental results of TCT current pulse shapes on samples after 1 MeV neutron irradiation and RT reverse anneal: a) no gamma radiation during the anneal (control) b) with gamma radiation during the anneal 5. Discussion 6. Summary Motivation of mixed radiations For the development of radiation-hard Si detectors for the SiD BeamCal program for the ILC In the ILC radiation environment, there will be gamma/e and neutron radiation Gamma irradiation is known to induce +SC in MCZ Si [1] The one year neutron fluence at the ILC is: ?neq = 2.68x1014 neq/cm2. The one year gamma radiation dose is 109 rads =103 Mrads. -SC by n and +SC by gamma may just cancel each other --- minimum net SC and Vfd! 1. Z.Li,et al.,IEEE Trans.Nucl.Sci.NS-51 (4)(2004)1901. Experimental: samples, radiations and measurements ? Samples: n-type MCZ Si, 390 μm, 0.25cm2, 1000 ?-cm, as-processed p+-n-n+ structure (processed at BNL) Radiations: Neutrons: 0.8-1 MeV (HF=1.3), 1.5-3x1014 neq/cm2, Annular Core Research Reactor in Sandia National Lab Gamma: 1.25 MeV 60Co, BNL, up to 500 Mrads ? Experimental technique: IV, CV, and TCT [2] wit