Edge defect analysis of high-strength corrosion-resistant steel.pdfVIP

BaosteelTechnicalResearch Volume9，Number3，September2015，Page23 Edgedefectanalysisofhigh—strength corrosion-resistantsteel DING Chen．HU Junliang．WANG WeianduU Gang ResearchInstitute，BaoshanIron SteelCo．，Ltd．，Shanghai201900，China Abstract：In thisstudy，a600 ~／IPa hot—rolled corrosion—resistantsteelplateproduced by a specificcompany is investigated．Edgejaggeddefectsandedgesurfacedefectsgeneratedonbothsidesofthestripduringproductionrae chraacterizedandanalyzed．Theresultsindicatethatthedistributionofreoxidationgranulesislocatedunderneath thesurfacepeeland thatcopper-containing grnaulesdiffuse along austenite grainboundaries．Thisphenomenon combinedwiththechemicalcompositionandproductionpraametersofastripindicatethatcopperbrittlenessleads toedgejaggeddefects．However，thesurfacedefectsshouldbeattributedtoinherentdefectsonthesurfaceofthe strip．Measuresthatpreventsurface oxidation andcoppersegregation atgrain boundarieswould likely eliminate thesetwotypesofedgedefects． Keywords：edgedefect；high—strengthsteel；corrosion—resistantsteel；copperbrittleness doi：10．3969／j．issn．1674—3458．2015．03．004 Theedgedefectsdiscussedinthispaperconsist Thekeyparametersofproduction areasfollows： ofjaggedandsurfacedefects，whicharethemain the slab heating temperature is 1256 ℃ ．rough quality problemsin steelproduction．The defect— rollingexittemperature is1017℃ ．finish rolling forming process is quite complicated，and many entrytemperatureis943．2℃ ．exittemperatureis investigationshavebeenundertakenbothlocallyand 850℃ ．coilingtemperature is620℃ ，and finished abroad．The results differ on the basis of the stripis3．12InlTlthick． variation of the inherent materialproperties and A11the metallographic specimens were etched productionparameters，withtheformerincludingthe using4％ (massfraction1Nitalandexaminedusing internal porosity，subsurface bubbles，inclusions， a Leica 6