毕业设计（论文）_无机阻燃剂粉体研究.docVIP

中 文摘 要 本文主要研究了四种无机阻燃剂粉体，即氢氧化镁（MH）、滑石粉（Talc）、硼酸锌（ZB）、改性蒙脱土（OMT）在聚丙烯（PP）体系中阻燃协同效应。通过极限氧指数、垂直燃烧实验、锥形量热仪、差示扫描量热仪（DSC）等研究了材料的燃烧性能和结晶行为。结果表明滑石粉、硼酸锌和MH存在较好的阻燃协同效应，尤其是硼酸锌和MH并用时对PP能起到较好的阻燃效果，但是改性蒙脱土和MH的阻燃协同效应效果不是很明显。DSC试验结果表明MH能起到异相成核作用，提高材料的结晶速率并降低材料的结晶活化能。作为无机阻燃剂粉体，MH具有广阔的应用前景。 关键词：聚丙烯、氢氧化镁、滑石粉、硼酸锌、蒙脱土、阻燃 Abstract In this paper, effect of inorganic flame retardants including magnesium hydroxide (MH), talcum powder (Talc), zinc borate (ZB) and surface-modified montmorillonite (OMT) on the flammability properties of polypropylene (PP) was investigated. Limited oxygen index tests, vertical combustion measure and cone calorimeter were employed to evaluate the fire retardancy and differential scanning calorimeter (DSC) of those materials. The results indicated that synergistic effect was occurred when Talc, ZB and MH were incorporated together into PP matrix. As an inorganic flame retardant, MH has the broad application prospect. The DSC results suggested that the MH have a remarkable heterogeneous nucleation effect in the polymer matrix and decreased the activation energy (ΔE) of the mentioned samples. Key Words: Polypropylene, magnesium hydroxide, talcum powder, zinc borate, montmorillonite, flame retardant. 目 录 第1章 文献综述 1 1.1 引言 1 1.2 聚合物的燃烧 2 1.3 阻燃剂的作用机理 3 1.3.1 冷却机理 3 1. 3.2 稀释机理 3 1. 3.3 隔离膜机理 3 1. 3.4 终止连锁反应机理 3 1. 3.5 协同作用机理 4 1.4 阻燃剂的种类 4 1.4.1 磷系阻燃剂 4 1. 4.2 金属氢氧化物阻燃剂粉体Al（OH）3和Mg（OH）2 5 1.5 聚烯烃/层状硅酸盐纳米复合材料 6 1.5.1 纳米复合材料的制备 6 1. 5.2 纳米复合材料的性能 8 1. 5.3 纳米复合材料的应用前景 8 1. 5.4 含有MH的高分子子材料 9 1.6 研究主要内容 9 1.7 研究的目的和意义 10 第2章 实验部分 11 2.1 材料制备 11 2.1.1 实验原料 11 2. 1.2 实验仪器 11 2. 1.3 实验步骤 11 2.2 性能测试 12 2.2.1 燃烧性能测试 12 2. 2.2 锥型量热计试验 15 第3章 氢氧化镁阻燃聚丙烯复合材料 16 3.1 MH对PP性能的影响 16 3.1.1 MH对PP/MAPP燃烧性能的影响 16 3. 1.2 Mg(OH)2的阻燃机理讨论 16 3.2 Talc协效对PP/MAPP/MH性能的影响 17 3.2.1 MH/Talc比例对燃烧性能的影响 17 3. 2.2 Talc含量对阻燃性能的影响 17 3.3 OMT协效对PP/MAPP/MH性能的影响 19 3.3.1 MH/OMT比例对基材燃烧性能的影响 19 3. 3.2 MH/OMT体系阻燃机理的讨论 20 3.4 ZB协效对PP/MH性能的影响 20 3.4.1 MH/ZB比例对基材燃烧性能的影