不锈钢技术及其发展详解.doc

不锈钢技术及其发展 摘要:不锈钢是工业与民用建筑中泛应用的金属材料，按其组织状态分为马氏体不锈钢、铁素体不锈钢、奥氏体不锈钢、双相不锈钢四种类型。目前不锈钢冶炼技术已从一步法、二步法发展到三步法冶炼，生产工艺趋于成熟，钢种结构更加合理，市场应用更加广泛，需求已从民用转向工业应用，是国民经济中不可替代的产品。 关键词:不锈钢;技术;发展 STAINLESS STEEL TECHNIQUE AND ITS DEVELOPMENT Abstract: Stainless steel is one metal material extensively applied in industrial and civil arc;hitec;ture. Ac;c;ording to structure it c;an he divided into four kinds: martensite, ferrite, austenite and duplex stainless steel. At pres-ent its smelting technique has been developed from one-tep, two-tep to three-tep method, production technology has been nearly ripe, grade composition more reasonable, market application even more wide sprea-ding, and demand for it had been changed from civil to industry. It is a kind of product could not being re-placed in national economy Key Words: stainless steel; technique; development 1前言 不锈钢是指具有抵抗大气、酸、碱和盐等腐蚀作用的合金钢的总称。通常所说的“不锈”是指其抗腐蚀性能，可归因于在氧化的环境中，形成一层氧化铬表面膜。这层薄膜具有不溶解、能自行恢复和无气孔的特点。 不锈钢具有良好的耐腐蚀、耐高温、耐磨损、外观精美等特性，用途非常广泛，是石油、化工、化肥、制药、食品、国防、餐具、合成纤维和石油提炼等行业中广泛使用的金属材料。 2不锈钢的种类和特点 不锈钢有两种分类法:一种是按合金元素的特点，划分为铬不锈钢和铬镍不锈钢;另一种是按在正火状态下钢的组织状态，划分为M不锈钢、F不锈钢、A不锈钢、A一F双相不锈钢。 2.1马氏体不锈钢 马氏体是奥氏体通过无扩散型相变而转变成的亚稳相，具有铁磁性，其硬度、强度主要由过饱和的碳含量决定，随着碳含量的增加，y相区边界逐渐向高铬方向扩展，而铬含量的增加，又稳定铁素体和缩小奥氏体y相区，并阻碍冷却时奥氏体向马氏体的转变，所以提高铬含量时，还需相应提高碳含量来扩大y相区，才能获得马氏体组织。典型的马氏体不锈钢有1 Cr13 -4Cr13和9Cr18等。1Cr13钢加工工艺性能良好，可不经预热进行深冲、弯曲、卷边及焊接;2Cr13冷变形前不要求预热，但焊接前需预热。1Cr13 ,2Cr13主要用来制作耐蚀结构件，如汽轮机叶片等，而3Cr13 ,4Cr13主要用来制作医疗器械外科手术刀及耐磨零件，9Cr18可做耐蚀轴承及刀具。 2.2铁素体不锈钢 铁素体是指铁和其它元素形成的体心立方晶格结构的固溶体。对一般钢而言，通常是指碳和其它元素在a铁中的间隙固溶体(a相)组织，不会发生奥氏体相变。铁素体不锈钢则是指含有大于12%的铬在a铁中的间隙固溶体。其中还含有相当低的碳和铁素体形成元素，如Al, Mo等，以保证钢的组织主要是铁素体，它具有强烈的磁性，不能用淬火方法使之硬化。铁素体不锈钢的含Cr量一般为13%一30%，含碳量低于0. 25%，有时还加人其它合金元素，金相组织主要是铁素体，加热及冷却过程中没有a -y转变，抗氧化性强。同时，它还具有良好的热加工性及一定的冷加工性。铁素体不锈钢主要用来制作耐蚀性要求较高而强度要求较低的构件，广泛用于制造生产硝酸、氮肥等设备和化工使用的管道等。 铁素体不锈钢不含镍或仅含少量的镍，因而是一种节镍不锈钢，随着对铁素体不锈钢的深人研究和应用实践，不锈钢生产和应用技术不断进步和完善，采用近代不锈钢生产技术所生产的低碳、氮，超低碳、氮，以及高纯[C+N}(100一150) x 10一6]和超级(Cr+3.3Mo}35)铁素体不锈钢等现代铁素体不锈钢，与用电弧炉单炼并加工生产的传统(普通)铁素体不锈钢相比较，性能上的某些不足已经得到了极大程度的克服和相当