裘凯锋毕业论文(终稿)教案分析.docVIP

摘 要 金属的热腐蚀是高温腐蚀的一种重要形式。热腐蚀是金属材料在高温含腐蚀性气体工作条件下与沉积在其表面的盐发生反应而引起的高温腐蚀形态。 本论文研究M17合金的腐蚀性能影响。采用离子技术在M17上，并将M17在900℃的50h的高温腐蚀。实验中采用的腐蚀介质为质量分数为75%（Na2SO4+10﹪K2SO4）+25%NaCl按1.2～1.6mg/cm2的涂盐量和后在同一温度进行50h的热腐蚀利用电子分析天平，金相显微镜(OM)分析M17抗腐蚀性能。实验结果表明15h后，表面氧化层脱落严重，而搪瓷涂层的失效则在40h之后。 关键词：等离子喷涂；搪瓷涂层； Abstract The metal heat corrosion of high temperature corrosion is an important form of. Heat corrosion is the metal material in high temperature corrosive gas work conditions and deposition in the reaction of the surface salt and cause of high temperature corrosion form. This thesis research to the M17 alloy enamel coating corrosion performance impact. Use ion spraying technology in the M17 alloy form a certain thickness enamel, will M17 alloy and enamel coating with the M17 alloy in 900℃ constant temperature under the environment of high temperature corrosion of 50 h. In the experiments of corrosive medium for quality score of 75% (Na2SO4 + K2SO4) + 25% NaCl, of which the quality of sodium and potassium sulfate points than then sulphonating agent. Will M17 and enamel coating to press 1.2 ~ 1.6 mg/cm2 coated in the specimen surface at the same temperature after 50h of heat corrosion. Use electronic analytical balance, metallographic microscope. The corrosion resistant properties of enamel comprehensive analysis. The experimental results show that the enamel coating spray is the M17 corrosion resistance ability to a much higher than the original base material. The original base material in the heat corrosion sulphonating agent after15 h, the surface oxidation layer falls off serious. But the failure of the enamel coating was in after 40 h. Keywords：Plasma spraying, Enamel coating, Hot corrosion目 录 摘 要 I Abstract II 第1章 绪论 1 1.1 金属腐蚀控制技术 1 1.1.1阴极保护 1 1.1.2 阳极保护 1 1.1.3 金属镀层和包覆层 2 1.1.4 涂层 2 1.1.5 加入缓蚀剂 2 1.2热腐蚀的机理 3 1.2.1热腐蚀的分类 4 1.2.2热腐蚀的特征 4 1.3 离子喷涂工艺的发展 4 1.4 离子喷涂发展趋势 5 1.4.1离子喷涂原理 6 1.4.2离子喷涂技术的主要特点 6 1.5离子喷涂搪瓷涂层的研究现状 7 1.5.1 搪瓷简介 7 1.5.2搪瓷涂层的国内外发展 7 1.6 本课题研究目的和主要研究内容 9 第2章 涂层制备