聚四氟乙烯解说.ppt

第二章热塑性塑料 第七节 聚四氟乙烯(polytetrafluoroethylene) 7.1 聚四氟乙烯的定义与聚合 7.2聚四氟乙烯的结构（重点） 7.3 聚四氟乙烯的性能（重点） 7.4 聚四氟乙烯的应用和改性 7.1 聚四氟乙烯的定义与聚合 一 定义 聚四氟乙烯树脂是四氟乙烯的均聚物， 其英文名称是polytetrafluoroethylene ，缩写为PTFE，分子结构式 Polytetrafluoroethylene is better known by the trade name Teflon?. Its used to make non-stick cooking pans . 聚四氟乙烯发明和发展 Polytetrafluoroethylene is one of the amazing accidental discoveries of science. One chemist at DuPont who was working on the project was named Roy Plunkett. Know him? One day Roy Plunkett opened up a brand new tank of tetrafluoroethylene gas, and nothing came out! He weighed it, and sure enough it was full. So he sawed the tank open and found a white powder where the gas was supposed to be. That powder, of course, was PTFE, polymerized from tetrafluoroethylene gas. This is the kind of accident that makes science fun. There are kinds of accidents in science which arent fun, say, those that involve large explosions and huge clouds of toxic gasses, but we wont talk about those right now. The fun kind of accident, which all scientists hope for, is an unexpected discovery which opens up a whole new area of investigation. This kind makes you famous and gets you lots of research grants, if you work at a university 一 PTFE的聚合 1. 单体制备 四氟乙烯单体易爆、易自聚。储存时应该避免与氧接触、并加入阻聚剂。 2. 聚合方法 本体聚合，但易爆聚——工业上不采用。 悬浮聚合，可得粒径为35～500μm的PTFE树脂颗粒。 乳液聚合，可得粒径更小的PTFE树脂颗粒。乳化剂:全氟辛酸胺。 7.2 PTFE的结构 一 链构象结构 1. 原子半径和范德华半径 2. PE与PTFE化学结构对比 PE的分子结构式 H原子范德华半径：0.12nm PTFE的分子结构式 F原子范德华半径：0.135nm PE分子的平面锯齿形构象 0.135×2＝ 0.27 nm 0.2534nm 3. PTFE的链构象特征 F原子完全对称排列，PTFE是非极性聚合物。 C—F键的键能高（487kJ/mol, C—C键的键能为387kJ/mol)，具有极高的化学稳定性。 3. PTFE的链构象特征 F原子的半径是0.064nm，而C—C键的键长是0.136nm，通过螺旋形构象形成的F原子“筒状外壳”严密的屏蔽了分子骨架碳原子。 3. PTFE的链构象特征 F原子的范德华半径0.135nm，在PTFE中两个F原子的距离是0.27nm，因此PTFE螺旋形构象链的刚性很强，难弯曲。 PTFE的分子量高，且几乎无支链 4. PTFE的聚集态结构 结晶度高，一般在55～75％范围，最高可达93～97％。 低于19oC时是三斜晶形；高于19oC时是六方晶系，熔点为320～345oC。 玻璃化转变温度（Tg）：-120、-65oC（120oC）。 是大量结晶区和少量无定形区并存的聚合物。 7.3 PTFE的性能 一 PTFE的基本特征 PTFE是白色不透明的蜡状粉末，密度为2.14～2.20g.cm-3，是树脂材料中最