提高无铅玻璃化学稳定性的论述.docxVIP

PAGE  提高无铅玻璃化学稳定性的研究 摘 要 本论文是对无铅玻璃化学稳定性提高的研究。根据我公司目前的工艺技术和综合考虑提出对无铅玻璃加入一定量的辅助物质对其化学稳定性的影响。如碎玻璃的加入量，退火制度的控制，在以往的经验，对比和实际实验中设计出了与传统不同的原料加入量特别是碎玻璃的加入，对其化学稳定性有一定的提高 本设计主要介绍本公司在配合料中碎玻璃的加入对其化学稳定性的影响，与传统不同本公司向配合料中稍加大了碎玻璃的量，经过试验和相关数据证明并没有使其化学稳定性降低反而有了一定的提高，并且节省了成本，减少了氮氧化物的排放从而减少了企业对环境的污 目前还没有提出配合料中碎玻璃加入50%的单位.综述我们对配合料中碎玻璃的加入量加大也是有一定价值和前景的！ 关键词：化学稳定性 碎玻璃 实验 Abstract In this paper, lead-free glass of research to improve chemical stability. According to my companys current technology and comprehensive consideration of lead-free glass made by adding a certain amount of supporting material for its chemical stability. Such as the amount of broken glass, annealing of the control system, in the past experience, contrast and the actual design of the experiment with the traditional raw materials by adding different amount of broken glass in particular, the addition of certain of its chemical stability of the raise Introduces the design of the material in the broken glass with the addition of the effects of their chemical stability, and tradition with a different material to the Company a little bigger amount of broken glass, after testing and related data to prove that did not make it reduce the chemical stability of the raise it to a certain extent, and cost savings, reduced emissions of nitrogen oxides in order to reduce the corporate pollution on the environment There is no material to tie in with broken glass by adding 50% of the units. Summary of our material with the addition of broken glass is also a certain amount of increased value and prospects! Key words: chemical stability of broken glass test 目 录 1 前言……………………………………………………………………………………1 2原料……………………………………………………………………………………3 2.1配合料………………………………………………………………………………4 2.1.1配方计算……………………………………………………………4 2.1.2碎玻璃………………………………………………………………7 2.1.2.1碎玻璃的粒度……………………………………………………………8 2.1.2.2碎玻璃的使用管理……………………………………………………….8 2.1.2.3碎玻璃的处理……………………………………………………………8 2.1.2.4配合料中的碎玻璃………………………………………………………8 2.1.2.5使用碎玻璃的实践………………………………………………