金泥精炼提纯工艺优化实践.docVIP

PAGE  PAGE 5 金泥精炼提纯工艺优化实践 魏克帅作者简介：魏克帅（1986-），男（汉），湖南道县，硕士，选冶厂厂长。 ，蔡建新，衡振平，彭湘林，党瑞峰 （中国地质矿业总公司,北京 100029；郑州金泉矿冶设备有限公司，郑州 450000） 摘要：介绍了采用化学精炼流程对某铜锌金银矿选冶厂的原电解法金泥提纯工艺进行改造与优化的生产实践。实践表明，此次工艺改造与优化是十分成功的。采用该工艺，成品金、银的纯度分别可达99.9%和99.2%以上，金直收率96.86%、银直收率93.4%以上，且经济效益显著。 关键词：金泥 精炼 提纯 金锭 The Optimization Practice of Gold Refining Process Wei KeShuai1 Cai JianXin Heng ZhenPing Peng XiangLin Dang RuiFeng (China National Geological Mining Corporation，BeiJing 100029, China) Abstract: This article introduced the modification and optimization of the original electrolytic gold refining process in a copper zinc gold silver processing plant by adopting chemical process. The actual production shows that, the modification and optimization is very successful. The purity of final gold and silver products can reach above 99.9% and 99.2% respectively, and the direct recovery of gold and silver can reach more than 96.86% and 93.4% respectively by using the new refining process, and it can make remarkable economic benefit. Key words: Gold mud,Refining,Purification,Gold bar 1 引言 近年来，随着国际经济形势的日趋严峻，大宗商品价格的不断下跌，这对国内外黄金企业无疑造成了巨大的冲击。在这种严峻的形势下，对金银产品进行精炼提纯，以提升其市场竞争力，则成为所有黄金企业迫在眉睫的任务[1]。 中国地质矿业总公司沙特分公司的铜锌金银矿选冶厂是一个处理能力为2200t/天的小型选冶厂，其冶金车间的设计处理能力为1800t/天，每月出厂合质金锭为400kg左右。该厂原设计的冶金工艺流程为氰化浸出-锌粉置换-电解法提纯-合质金锭熔炼，由于粗金泥中的金银含量偏低，采用该工艺对锌粉置换后的粗金泥进行精炼提纯效果非常差，提纯后的金泥中金含量不到2%，银含量低于20%，合质金锭产品中金+银含量仅21.3%，远低于金+银含量＞90%的设计指标。此类合质金锭产品基本无法出售，致使该厂冶金车间的产值几乎为零。 因此，为保证该厂冶金车间生产出合格的金银产品、为选冶厂创造产值、为公司创造效益，采用一种技术指标先进、工艺流程合理、经济效益好的金泥精炼提纯工艺对原有工艺进行改造与优化则是势在必行[2]。 2 金泥精炼提纯工艺的改造与优化 2.1 工艺流程 此次金泥精炼提纯工艺的改造与优化综合考虑了投资成本、设备场地、粗金泥性质、生产周期和流程的操作难度等各方面因素，最终决定选用盐酸-硝酸两步除杂的化学精炼工艺，工艺流程如图1所示。 滤液 沉银 还原 铸银锭 银产品 铸金锭 金产品 还原 滤液 熔炼 盐酸除杂 合金水淬 硝酸除杂 粗金泥 滤液 熔炼 盐酸除杂 合金水淬 硝酸除杂 粗金泥 王水溶金 还原 图1 金泥精炼提纯工艺流程图 Fig.1 Gold Refining Process Flowsheet 2.2流程的基本原理 （1）盐酸除杂。利用在加热的条件下，金泥中的锌、铅、铁等贱金属可以和稀盐酸反应，生成可溶性盐，而金、银、铜不溶于稀盐酸的原理，将金银铜合金和杂质分离。 Zn+2HCl＝ZnCl2+H2↑ Pb+2HCl＝PbCl2+H2↑ Fe+2HCl＝FeCl2+H2↑ （2）熔炼。金泥在高温环境（1200 ℃ 以上）下会熔解成液态，部分杂质如硫（444 ℃ ）、铅（850 ℃