材料的热稳定性.pptVIP

2.5 材料的热稳定性(Thermal Stability) 2.5.1 热稳定性的定义 ;Thermal Shock Stress leading to the fracture of brittle materials can be introduced thermally as well as mechanically. When a piece of material is cooled quickly, a temperature gradient is produced. This gradient can lead to different amounts contraction in different areas. If residual tensile stress becomes high enough, flaws may propagate and cause failure. Similar to behavior can occur if a material is heat rapidly. This failure of a material caused by stresses introduced i by sudden changes in temperature is known as thermal shock.;热稳定性的表示方法;材料在未改变外力作用状态时，仅因热冲击而在材料内部产生的内应力成为热应力。 Stresses introduced into a material due to differences in the amount of expansion or contraction that occur because of a temperature. ;热应力产生原因 (1)构件的热膨胀或收缩受到约束时造成热应力； (2)相连接的构件存在温度差，构件间相互约束造成热应力； (3)构件本身存在温度梯度，其间各部分相互约束造成热应力； (4)不问构料的组合和约束造成热应力 Thermal Stress Strain Thermal stress and strain are caused by temperature change. Materials expand at temperature increase and contract at temperature decrease. Restricting thermal strain cause thermal stress.;Thermal Strain;Thermal Stress;对于脆性材料，从弹性力学出发，采用应力-强度作为判据，可以分析材料热冲击断裂的热破坏现象。;可见， 越大，则材料能承受的温度变化越大，热稳定性也就就越好。;第一热应力断裂抵抗因子R(Thermal Shock Parameter);考虑承受的最大温差与最大热应力、材料中的应力分布、产生的速率和持续时间，材料的特性（塑性、均匀性、弛豫性），裂纹、缺陷、散热有关。;? 材料的热导率kt：热导率越大，传热越快，热应力持续一定时间后很快缓解，对热稳定性有利。 ? 传热的途径：材料的厚薄2rm，薄的材料传热途径短，易使温度均匀快。 ? 材料的表面散热速率：表面向外散热快，材料内外温差大，热应力大，引入表面热传递系数h------材料表面温度比周围环境高单位温度，在单位表面积上，单位时间带走的热量（J/s·cm2·oC)。 影响散热的三方面因素，综合为毕奥模数?=hrm/?，无单位。 ?越大对热稳定性不利。;2.5.3 抗热冲击损伤性;从断裂力学的观点出发以应变能-断裂能为判据。 材料中微裂纹扩展、蔓延的程度，积存的弹性应变能、裂纹扩展的断裂表面能影响材料的抗热损伤性。 积存的弹性应变能较小，材料的扩展小；裂纹扩展的断裂表面能大，裂纹的蔓延程度小。;抗热应力损伤性正比于断裂表面能，反比于应变能的释放率。 R4?E/?2(1－ ?) 材料弹性应变能释放率的倒数，用于比较具有相同断裂表面能的材料。 R5?E×2 ?eff/?2(1－?) 用于比较具有不同断裂表面能的材料。 强度高的材料原有裂纹在热应力的作用下容易扩展蔓延，对热稳定性不利。; Thermal Shock behavior is affected by following factors: Coefficient of thermal expansion Thermal conductivity Modulus of el