jiangqi技术人员专业培训1-配方入门简化版要点分析.ppt

* 华谊集团 双钱股份 * 提问？ 以上这些配方设计内容，可以保证设计出很好的钢丝帘布胶配方，这样的轮胎在带束层、胎体部位是完美的吗？ 我们要知道钢丝的裁断面是没有镀层的。前面所讲的内容都是针对钢丝的镀层而言。ZERO Cu/Zn, ZERO ADHESION. * 华谊集团 双钱股份 * 注意帘线 的截断面 * 华谊集团 双钱股份 * 轮胎带束层示意图 使用前 使用后 胎体帘布反包端点 也是同样的问题 * 华谊集团 双钱股份 * 轮胎行驶肩部、胎圈这两个位置损坏最多。 因此钢丝帘布的包边胶、夹胶、胎面覆皮等是非常重要的。 我们所做的是如何延迟损坏、减少损坏，而不是杜绝损坏。 破坏能、生热 粘合性能 自粘性…… * 华谊集团 双钱股份 * 结束语 配方设计要考虑各类原材料的性能，并综合选择。 胶料物性是配方设计的最终目标，以简单有效为本。 轮胎技术在不断更新，新材料的应用有待抓紧开发。 了解轮胎损坏的原因，有助于配方开发。 * 华谊集团 双钱股份 * END 谢谢 * * When brass-coated wire is drawn during the forming process, Zn2+ ions diffuse to the surface and are oxidised to form a ZnO layer. A thin CuO skin can form, but it is usually present in very small amounts. The enriched ZnO layer also contains metallic copper inclusions, formed as a result of the internal oxidation mechanism of zinc. Variable wire drawing conditions may affect the thickness and distribution of ZnO, as well as the number of copper inclusions. During vulcanization, the brass surface is exposed to active sulphur-containing molecules present in the rubber compound and a strong bond is formed between the rubber compound and the tyre cord by the action of an interfacial; non-stoichiometric CuxS layer x ? 1.8 that grows before the rubber is fully cross-linked. * * * The depth profile for the sample containing 901 is very similar to that containing 680C; the only clear and significant difference being the much higher level of cobalt within the interfacial layers of copper sulphide and zinc oxide. Note the depth of penetration is much larger also. It is possible to explain the fact that more cobalt is delivered to the interface, perhaps by a faster dissociation rate of the cobalt boroacylate of 901. Therefore, it can be incorporated more efficiently into the copper sulphide and zinc oxide lattice, filling vacant sites in the copper sulphide and interstitial sites in the zinc oxide lattice. * The depth profile for the cobalt stearate shows that the cobalt distribution is not so large as that shown by the 680C