高炉矩阵下载论文.docVIP

济钢1#1750m3高炉布料矩阵的探索实践 韩俊杰，法泉营，刘德楼，李传辉 （济南钢铁集团总公司，山东 济南250101） 摘　要：济钢1#1750m3高炉开炉初期，因受炉顶设备限制，只能使用单环布料，料面堆尖高，气流不稳定。改为组合双环布料后，因角差大，档位小，不利气流调整。设备故障消除后，探索出了适应炉况顺行的多环布料矩阵，高炉利用系数达到了2.37t/m3.d。 关键词：高炉；布料矩阵；多环布料；料面形状中图分类号：TF543　　 文献标识码：A　　 文章编号：1004-4620（2005）03-0010-02 Exploring Practice of Burden Distribution Matrix of Jigangs 1#1750m3 BF HAN Jun-jie, FA Quan-ying, LIU De-lou, LI Chuan-hui （Jinan Iron and Steel Group Corporation, Jinan 250101, China） Abstract：Because of the restriction of equipment in the roof, single ring distribution only can be used at the beginning of 1750m3 BF blow on, then charge level accumulates, air current doesnt steady. After mending, double rings distribution is used but presenting the big gap angle and small hiberarchy, and then being disadvantage for air current adjusting. Many rings distribution suiting regular working is began to try after removing equipment failure. Therefore the utilization coefficient is up to 2.37t/m3.d. Keywords: blast furnace；burden distribution matrix；many ring distribution；feed influent track 1 前? 言 　　济南钢铁集团总公司第一炼铁厂（简称济钢第一炼铁厂）1#1750m3高炉于2003年9月1日开炉，因炉顶设备缺陷、风机故障、热风管道膨胀器等影响，一直没能找到合理的操作炉型。随着设备故障的排除和操作技术的改进，逐渐找到了相对合适的布料制度。 2 布料矩阵的探索历程 2.1 单环布料和组合双环布料　　开炉初期，由于炉顶设备的限制，无法实现多环布料，只能使用单环布料。因为济钢首次使用无料钟炉顶进行单环布料，主要模仿钟式布料，但在炉喉间距较大、料面堆尖较高的情况下，料面不稳定，易出现中心管道，导致风压突升悬料。透气性整体上看起来虽然比较高，但压量关系不稳定。此外，多次坐料很容易造成炉缸堆积和炉墙结厚，尤其是开炉初期不利于合理操作炉型的形成。经过对上料系统的改进，尤其是对上料程序和装料程序的优化，并根据无料钟炉顶参数（见表1）及开炉初期测定的料面和料流轨迹情况（见表2、表3），选择两组比较合理的数据，即在一个布料周期内，间隔执行两个不同的单环矩阵，称为组合双环布料。但组合双环布料，料面会有一定程度的重合，既不利于气流通道的形成，也不利于气流的调整，每次调矩阵后，在新的气流通道形成之前，旧的通路已经被堵死，易悬料，不利于维护炉况顺行。 表1? 无料钟炉顶参数 项目 参数 项目 参数 设计炉顶压力/Mpa 0.2 上、下料罐容积/m3 40 溜槽倾动速度/r.min-1 0.2667 溜槽回转速度/r.min-1 8 溜槽长度/mm 3400 溜槽倾动范围 2°～43° 上料闸直径/mm 1100 上密封阀直径/mm 1300 料流调节阀直径/mm 750 下密封阀直径/mm 900 炉喉直径/m 6.8 炉喉高度/m 1.5 表2? 焦炭各档位对应角度 1.0m料线 1 2 3 4 5 6 7 8 9 10 11 α角 10.2 19.1 22.8 26.7 29.8 31.7 33.5 35.7 37.6 39.2 42.1 表3? 矿石各档位对应角度 1.0m料线 1 2 3 4 5 6 7 8 9 10 11 α角 110 18 21.5 24.3 26.5 28.5 30.7 32.3