防水混凝土的实用原则 　　【摘 要】 随着国民经济的高速发展，大、中城市的高层、超高层建筑应运而生，而这些建筑的地下占地也不断增加，对其使用功能的要求也随之提高，因此地下建筑部分的防水防渗功能就显得非常重要。影响防水混凝土抗渗性的因素较多，只要切实掌握配制原则，就不难配制出质量良好的防水混凝土。本文就不同砂石级配怎样配制出抗渗能力较高的防水混凝土做简单的介绍。 　　【关键词】 防水混凝土 配置原则 砂石级配 　　【Abstract】 Along with the rapid development of national economy， large and medium sized cities high-level， high-rise building emerges as The Times require， and the construction of underground covers also continue to increase， increases to its use function request， so the underground parts of the waterproof function of seepage control is very important. Factors affecting the permeability resistance of waterproof concrete is more， as long as be mastered preparation principle， it is not hard to make a good quality of waterproof concrete. In this paper， the different aggregate gradation how to formulate the permeability resistance of high waterproof concrete do simple introduction. 　　【Key words】 waterproof concrete， sandstone distribution， configuration principle 　　随着国民经济的高速发展，国家土地资源日趋紧张，高层建筑应运而生，而这些建筑的地下占地也愈来愈大，对其使用功能的要求也随之提高，地下建筑部分的防水防渗功能尤显重要。所以，防水混凝土不仅用于疏水、储水构筑物而更用于地下建筑。 　　近年来，有关方面为揭示防水混凝土的防水原理，确立我国自己的防水混凝土配制理论进行了大量的科学试验和工程实践，认为配制防水混凝土的技术关键在于提高砂浆质量、增加砂浆数量抑制，调整配合比，减少混凝土内部空隙，改变空隙特征，提高自身密实度和抗渗性。 　　有人认为，要配制高密度混凝土，必须采用理想的砂石级配。实际上砂石级配对混凝土的空隙率和抗渗性影响不大，改变砂子级配，砂子空隙率仅变化1～3%，然而，在实践中我们发现不同砂石级配同样能配制出抗渗能力较高的防水混凝土。关键是应该遵循防水混凝土的一些配制原则。 　　1 降到水灰比，控制塌落度 　　混凝土拌和物的水灰比对硬化混凝土空隙的大小、质量起决定性作用，直接影响着混凝土结构的密实性。从理论上说，在满足水泥完全水化前提下，水灰比越小，混凝土密实性越好，抗渗性及强度也越高。若水灰比过大，超过了水泥保水限度则会出现析水想象。 　　渗透速度与水灰比大小也有很大关系，渗透系数将水水灰比的增加而增大，当水灰比从0.4增至0.7时，渗透系数增大100倍以上。 　　考虑到施工现场与试验室的差别以及防水混凝土的抗渗压力不应小于6公斤/厘米2的要求和耐久性的要求，防水混凝土最大水灰比不宜超过0.60。 　　在相同水灰比和含砂率条件下，塌落度不同泌水率有明显差异，也会导致抗渗性不同。塌落度大，泌水率越大，骨料的沉降作用越强烈，混凝土内开放性毛细孔也越多，必然会对混凝土的渗透性产生一定影响。因此，在要求选择适宜水灰比的同时，必须控制混凝土塌落度。从便于施工和确保混凝土的抗渗性考虑，普通防水混凝土的塌落度以3～5厘米为宜。 　　近年来，减水剂的应用，使普通防水混凝土的塌落度突破了上述限值，获得了良好的抗渗性。 　　2 适当提高水泥用量、砂率及其相应的灰砂比 　　在适宜的水灰比范围内，水泥用量和砂率对混凝土抗渗性具有明显的影响。应采用较高的砂率和水泥用量，砂子和水泥的用量比例必须协调。砂子用量过多，水泥浆不够包裹砂子，混凝土结构不密实，不仅降低了抗压强度，且引起了抗渗性的急剧下降。若水泥用量太大，不仅增加工程造价，而且混凝土拌合