上海某吹填场地砂土固化试验分析.docVIP

上海某吹填场地砂土固化试验分析 　　摘要：固化方法是目前把转化为可用土资源常用的方法土壤固化剂是一种显著的改变土壤物理力学性能，使之成为相对强度高、收缩量小、压实度高、不会出现“再次泥化现象”的新型工程材料。本文对上海某吹填场地砂土中添加固化剂后形成的固化土在室内开展了一系列工程特性试验研究，并得到了固化土的压缩模量、抗剪强度与掺量、养护龄期之间的关系。根据室内试验结果，就不同固化剂、掺量和养护龄期对加固土压缩模量和抗剪强度的影响进行分析。 　　关键词：固化剂掺量龄期压缩模量抗剪强度 　　中图分类号：U41 文献标识码：A 文章编号：1672-3791（2015）01（c）-0000-00 　　Abstract：Pavement cement as component materials of concrete pavement，its property relates to service life and service level of cement concrete pavement.Through a series of the indoor experiments，the basic mechanical behavior of the solidified sandy soil was studied.The test results show that the modulus of compressionincreases logarithmically withmixing ratio andandshear strengthlinearlyincreases withcuring age.The variation of modulus of compression and shear strength of Hengshasandy soilstabilized by solidified agent WG-K1 and self-definedwith different mixing ratio and curing age are studied through the laboratory experiment in this paper . 　　Key words：solidified agent；mixing ratio； curing age；modulus of compression；shear strength 　　1 前言 　　软土加固的目的是改善土的变形和强度。正在研究与工程上实际使用的加固方法一般可归纳为物理方法， 化学方法、物理―化学方法[1]。就发展趋势来说，物理-化学方法最有前途，可从本质上改变土的工程性质。而固化剂作为一种新型材料，在国内也逐渐被广大工程人员接受和认可。固化技术已在国外开展了一些研究和使用[2，3]，目前在国内的研究正处于起步阶段。因国内许多建设项目分布在软土和不良地区， 对于固化剂加固软土的工程性能的分析则有着非常现实的意义[4]。 　　本文取用上海某吹填场地砂土， 采用固化剂WG-K1 和自配固化剂， 对其加固土的压缩模量和抗剪强度的变化规律及不同掺量比和龄期时的关系的变化进行了分析。 　　2 试验条件 　　2.1 试验用料 　　试验用料包括固化剂WG-K1、自配固化剂、普通硅酸盐水泥、自来水和土样。 　　2.2 试样制作及养护 　　试验土含水率取40%，固化剂WG-K1掺量为0.8%，1.2%，1.5%，自配固化剂掺量为8%，10 %， 12 %，龄期分别为7， 15， 30d。试验中，土和固化剂需在土工搅拌机中搅拌2-3分钟直至拌合均匀。搅拌后的拌合土需填入环刀内塑形，环刀内壁上预先涂上一层凡士林以便于脱模。试验采用养护箱养护，置入20 ℃、湿度96%的养护箱内进行养护直到达到养护龄期。 　　2.3主要仪器设备 　　直剪仪， 拉杆式固结仪。 　　因固结试验快速法可得到与常规试验近似的结果[5] 。所以试验中采用快速法。直剪试验按土工试验方法标准[6]进行。 　　3 试验结果与分析 　　3.1固结试验 　　WG-K1固化土和自配固化土不同掺量的压缩模量见图1和图3。两种固化剂的压缩模量Es与固化剂掺量的关系以对数曲线进行拟合的效果最好，三种龄期下趋势线的R平方值均超过0.99。这表明压缩模量与固化剂掺量的关系可视为对数型增加，对数拟合符合Es后期增速变缓的趋势。 　　图1WG-K1压缩模量与固化剂掺量关系 　　图2 WG-K1压缩模量与养护龄期关系 　　图3自配压缩模量与固化剂掺量关系 　　图4自配压缩模量与养护龄期关系 　　WG-K1固化土和自配固化土不同龄期的压缩模量见图2和图4。自配固化剂