高强钢热处理焊接头显微组织力学性能论文.docVIP

BWELDY960Q及20CrMnTi焊接接头组织和力学性能 【摘要】 对于工程构件,人们大多希望采用高强钢来降低材料的消耗,但对于高强钢的焊接的研究比较少,为了更好的开发国产高强钢的应用,研究这类钢的焊接接头的组织及力学性能的变化规律,很有实际意义。本文通过对上海宝钢生产的低碳高强钢板BWELDY960Q和锻造态20CrMnTi钢,用SLD-80焊丝和TUnion GM 100焊丝,采用CO2气体保护焊方法,研究了焊丝及热处理工艺对焊接接头的显微组织和力学性能的影响。研究结果表明：对于低碳高强钢板BWELDY960Q焊接接头而言,SLD-80和TUnion GM 100两种焊丝的焊接结果差别较大,采用SLD-80焊丝焊接后材料的综合力学性能较好；调质处理工艺(900℃×2h×油冷+650℃×lh×空冷)有效地改善了低碳高强钢板BWELDY960Q的综合力学性能,强度、硬度较调质处理前有所下降,但塑性、韧性显著提高,相比之下,SLD-80焊丝焊接件综合力学性能较好；对于SLD-80焊丝,退火处理使得低碳高强钢板BWELDY960Q焊接接头的力学性能得到明显的改善,其中经过550℃退火后,焊件的综合力学性能最好；20CrMnTi和BWLEDY960Q采用不同...?更多还原 【Abstract】 For engineering components, most people want to use high-strength steel to reduce material consumption, but there is less research about the welding of high-strength steel. In order to develop the application of high-strength steel preferablely, it has practical sense to investigate the microstructure and mechanical properties of weld joint for this kind of steel. Based on the low-carbon high-strength steel BWELDY960Q and forging state 20CrMnTi produced by Shanghai Baosteel, with the SLD-80 weld...?更多还原 【关键词】 高强钢； 热处理； 焊接接头； 显微组织； 力学性能； 【Key words】 high strength steel； heat treatment； weld joint； microstructure； mechanical property； 摘要 5-6 Abstract 6-7 第一章 绪论 10-23 1.1 合金钢、低碳合金钢的概况 10-13 1.1.1 合金钢及合金元素 10-11 1.1.2 低碳合金钢的种类与应用 11-13 1.2 低合金高强钢的组织性能与发展 13-15 1.2.1 低合金高强钢的组织性能 13 1.2.2 国内外低合金高强钢的发展比较 13-14 1.2.3 低合金高强钢的新发展 14-15 1.3 锻造和热处理工艺对高强钢组织性能的影响 15-17 1.3.1 高强钢的锻造工艺及其对组织性能的影响 15-16 1.3.2 热处理对高强钢锻后组织及力学性能的影响 16-17 1.4 焊接和热处理工艺对高强钢组织性能的影响 17-22 1.4.1 高强钢的焊接工艺及其对组织性能的影响 17-19 1.4.2 热处理对高强钢焊接焊头组织及力学性能的影响 19-22 1.5 本课题的提出及意义 22-23 第二章 实验材料及方法 23-29 2.1 实验材料 23 2.2 实验设备 23-24 2.3 实验过程及方法 24-29 2.3.1 焊接板材的加工 24 2.3.2 材料的焊接工艺 24-26 2.3.3 材料的热处理工艺 26-27 2.3.4 力学性能测试 27-28 2.3.5 显微组织及断口观察与分析 28-29 第三章 实验结果及讨论 29-62 3.1 低碳高强调质钢板BWELDY960Q焊接接头的显微组织及力学性能