铸铝温度分布曲线.docVIP

铸铝在铸型中温度分布报告 材控04班 曲明阳 摘要：用描点作图法绘出铸铝件在砂型和金属型铸模（铸型壁均足够厚）中浇铸后0.02h、0.2h和0.5h时刻的温度分布状况，并作分析比较。 关键词：铸铝；浇铸;温度分布 A report of the temperature distribution of cast aluminum in the mold Qu ming yang Abstract: draw the temperature distribution of aluminum casting in sand mold and metal mold after casting 0.02h,0.2h and 0.5h with the trace point mapping method assume the mold wall are enough thick ,then analysis and comparison the temperature distribution. Key words: aluminum; casting；temperature distribution 铸件侧： a 690 ℃ 20 ℃ 带入得， 其中： a1，a2是铸件和铸型的热扩散率， b1，b2分别是铸件和铸型的蓄热系数。 取浇铸温度 690 ℃，铸型的初始温度为 20