铈对模具钢晶粒的影响.doc

铈对D6冷作模具钢晶粒度影响 摘要 本文研究了稀土Ce对D6钢的晶粒度和本质晶粒度（奥氏体晶粒长大倾向）的影响。取Ce质量分数分别为0.038%和0.073%的两种钢坯实验。D6钢为莱氏体钢，根据GBT6394-2002采用渗碳体网法测定了其本质晶粒度。用光学显微镜得到了金相图片。通过观察比较不同Ce含量晶粒度和本质晶粒度的大小，分析了Ce对D6冷作模具钢晶粒度的影响。 关键词: 冷作模具钢 晶粒度 本质晶粒度 稀土Ce 碳化物Effect of Ce on grain size of D6 cold-working die steel Abstract This paper studied the effect of Ce on grain size and inherent grain size (the tendency of austenitic grain growth) of D6 cold-working die steel. Two kinds of steel billet were used in this experiment with Ce mass fraction 0.038% and 0.073 % respec- -tively. Because D6 belongs to ledeburite steel, this experiment was conducted based on GB/T6394-2002 (cementite nets method), and inherent grain size was obtained. Metallographic photos were taken by optical microscope. The grain size and inherent grain size of D6 with different contents of RE Ce were observed, and analyzed the effect of Ce on the samples. Key works： die steel grain size inherent grain size Ce carbide1.1 模具钢简介 模具钢是用来制造冷冲模、热锻模压铸模等模具的。模具是机械制造、无线电、电机电器等工业部门中制造的主要加工工具。模具的质量直接影响着压力加工工艺的质量、产品的精度产量和生产成本、而模具的质量与使用寿命除了靠合理的结构设计和加工精度外，主要受模具材料和热处理的影响 图3.1稀土化合物的标准生成自由能与温度的关系图 3.1.2微合金化作用 ①细化奥氏体晶粒、细化碳化物。 RE元素溶入奥氏体，使钢的相变温度升高，C—曲线右移，促使奥氏体稳定，提高奥氏体晶粒粗化温度。 ②固溶度及固溶强化 稀土元素在铁液中与铁原子是互溶的，但其在铁基固溶体中的分配系数极小，因为稀土原子半径比铁原子大，是表面活性物质，因而在铁液凝固过程中，被固/液界面推移最后富集于枝晶间或晶界，对固溶体能提供强化作用[2]。 ③影响杂质元素的溶解度和减少脱溶量 稀土降低碳、氮的活度，增加碳、氮的溶解度，降低其脱溶量，使它们不能脱溶进入内应力区或晶体缺陷中去，减小了钉扎位错的间隙原子数目，因而提高了钢的塑性和韧性。另外，稀土影响碳化物的形态、大小、分布、数量和结构，提高了钢的机械等性能。 4.1 试验 为了验证Ce对D6钢晶粒度的影响，在试样中加入不等的铈，试样成分表如下 试样编号 C Cr W Si Mn S P Ce 1 2.03 11.35 0.66 0.31 0.35 0.010 0.021 0.038 2 2.03 11.35 0.66 0.31 0.35 0.010 0.021 0.073 表4.1 试样成分（质量分数，%） 同时按照以下步骤进行进行观测金相组织： ⑴ 取样。从试样1#和2#上分别切取10×10mm大小的试样； ⑵ 热处理。将切取的试样放入加热炉中并记好所放位置，防止热处理后试样上的记号消失，使试样混淆。然后加热至820℃,然后保温1小时，再随炉冷至600℃，最后空冷至室温。 5.1 Ce对晶粒度的影响 由实验观察得出的金相组织如下： a) 1号晶粒度 b) 2号晶粒度 图5.1 晶粒度比较（×50） a) 1号晶粒度 b) 2号晶粒度 图5.2 晶粒大小比较（×100） 由图可以看出，试样2的晶粒度比试样1的晶粒度明显细小均匀。也就是说Ce的加入量对D6钢的晶粒度有明显的影响，在适当的范围内，且