岳：CSP流程产无取向电工钢析出物计算档.docVIP

CSP生产无取向电工钢中AlN、MnS析出计算 岳尔斌项利 钢铁研究总院 连铸技术国家工程研究中心，北京100081） 摘 要： 关键词： ， ，Calculation on AlN and MnS Precipitation of Non-oriented Electrical Steel in CSP Process YUE Er-bin, XIANG Li , FAN Ding-dong, ZHAO Pei （National Engineering Research Center of Continuous Casting Technology, Central Iron Steel Research Institute, Beijing 100081，China）Abstract：Combining with the study of analogue experiments and test analysis, the kinetics of precipitation and growth of AlN and MnS non-oriented electrical steel in CSP process is calculated. The results show that the precipitating particles of AlN and MnS of typical grades non-oriented electrical steel in CSP process have grown more in soaking process, but the precipitation contents are less than 20% of total contents of nitride and sulfide. The precipitating particles of AlN and MnS have precipitated almost after the hot rolling process. The precipitation contents are more than 80% of total contents of nitride and sulfide, but it is too late for the precipitating particles to grow at the end of the hot rolling process. Keywords：CSP，Non-oriented electrical steel，Calculation AlN and MnS precipitation 前言 钢液在凝固时或固态温度降低时，由于某些元素(如硫、氮)溶解度下降而沉淀析出的化合物，如MnS、AlN等称为析出物。这些析出物的析出总量、析出方式、析出时间对无取向电工钢成品的磁性能有着重大的影响，因此有必要对析出物的析出规律加以研究。 无取向电工钢与CSP常规低碳钢产品相比，化学成分具有以下特点：C%极低，要求小于0.005％；S%含量更加严格，一般要求小于0.008％；Si%较高，例如W540，Si%要求在1.1～1.3％；Als%含量高，比常规CSP生产的低碳钢高10倍左右；N％含量要求0.005％。 关于钢中析出物热力学、动力学的研究，前人做了大量的工作，主要集中在铌、钒、钛的碳、氮化物析出形态、物理化学反应基础数据研究，部分研究者建立了析出物析出模型，并根据相关试验结果进行了修正，但是针对CSP工艺流程生产电工钢的析出物研究，尚不多见，文献报道亦较少。 本文以典型牌号无取向电工钢中的MnS、AlN%(Si+Al)与0.5%(Si+Al)试验铸坯的硫、氮、锰、铝元素控制水平和实际含量接近，计算化学成分取平均成分Al%=0.35，Mn%=0.30，S%=0.004，N%=0.003。 假设A: 假定在析出物的析出以及长大过程中奥氏体和MX界面组成达到局部平衡。假设B: 假定析出物为球形。假设C: 析出物形成元素M在奥氏体中的扩散为析出物长大的限制性环节。 (2)计算公式[1~5] 形核以及析出过程中的化学驱动力可以由式（1）计算。 （1） 式中： R──气体常数，J/（mol?K）； T──温度，K； ，──初始M、X的浓度； ，──平衡时M、X的浓度。 假定析出物为球形，则临界形核半径和临界形核功为： （2） （