新型醇基铸造涂料复合分散悬浮剂的研究 冯胜山 朱松林（湖北省机电研究设计院 武汉430070）　 摘要： 本文介绍了新型醇基铸造涂料复合分散悬浮剂的主要性能特点，对比研究了它的悬浮效果，论 述了它的作用机理。结果表明：新型醇基复合分散悬浮剂的耐火度高，抗裂性好，悬浮能力与有机膨润土相当；生产的醇基涂料悬浮率和抗裂性均达到了国际著名品牌涂料水平；静电分散稳定机理、空间位阻分散稳定机理和增粘机理的共同作用是其分散悬浮效果优良的主要原因。 关键词：铸造；醇基；涂料；分散；悬浮；机理 中图分类号：TG221 Research on the New Disperse-suspending Agent of Alcohol-based Cast-coating Feng Shengshan Zhu Songlin (Hubei Research Design Institute of Mechanical Electronic Engineering Wuhan 430070) Abstract The main technological properties of a new disperse-suspending agent of alcohol-based cast-coating are introduced in this paper. Its suspension effect is studied by comparing. Its mechanism is analyzed. The results show that refractory temperature of the new disperse-suspending agent is higher, the ability of preventing crack is powerful, its suspending stability is equivalent to organized bentonite,s, the abilities of suspending and preventing crack of alcohol-based cast-coating with the disperse-suspending agent are equivalent to the abilities of international distinguished coatings, the co-action of disperse-suspending mechanisms of electrostatics and space is the main cause. Key words foundry alcohol-based casting disperse suspend mechanism 醇基铸造涂料具有干燥快、生产效率高、适用范围广等特点，在我国铸造生产中已得到广泛应用。但是，目前国产的醇基涂料存在的问题较多，主要表现为分散悬浮稳定性差，涂料在长期存放和运输过程中易产生沉淀；其次是流变性，特别是流平性差，涂层刷痕严重，影响铸件的表面质量。 醇基涂料主要由耐火骨料、溶剂、分散悬浮剂、粘结剂等组成。良好的分散悬浮剂不仅能有效地保证涂料各组分的分散均匀性和涂料的悬浮效果，而且还能改善涂料的涂刷性，有利于施涂，提高涂层和铸件的表面质量。钠基膨润土是一种传统的醇基涂料悬浮剂，但它在醇溶液中溶胀性不好，分散悬浮效果差。采用季胺盐处理的有机膨润土是一种较好的醇基涂料分散悬浮剂，但它需用有毒的二甲苯引发，而且价格昂贵，另外发气量很大。采用锂盐与钙基膨润土进行阳离子交换处理制得的锂基膨润土在醇溶液中具有较好的分散悬浮性，但锂基膨润土吸水溶胀后，在醇溶液中稳定性较差，由于胶粒易脱水而使醇基涂料失去悬浮作用， 致使涂料中耐火骨料下沉结块，形成“死沉淀”，特别是在长期贮存或长途运输过程中，更为严重。此外，膨润土的耐火度低，热收缩率高，涂层抗裂性差。 因此，开发新型质优价廉的醇基涂料分散悬浮稳定剂势在必行。 我们采用一种特殊硅酸铝质粘土为基础材料，应用胶体化学的静电位阻分散稳定理论，以特殊复合电解质和高分子聚合物作为分散剂，并辅已多种附加物对其进行综合改性处理，开发出一种新型醇基复合分散悬浮剂，用于生产醇基系列涂料，取得了显著效果。这种新型醇基涂料复合分散悬浮剂已于1998年获得国家发明专利[1]。 1 新型醇基复合分散浮稳定悬剂的性能特点 新型醇基复合分散悬浮稳定剂的基础材料呈灰白色粘土状，其主要组成物是一种由二八 面体云母与二八面体蒙脱石组成的规则间层矿物，主要成分为SiO2和Al2O3，2.87g/cm