低碳钢钨极氩弧焊焊接参数对焊缝成型的影响.docVIP

摘要 主要研究低碳钢钨极氩弧焊焊接时，焊接电流、焊接速度、氩气气体流量等工艺参数对焊缝成型的影响。在反复调节不同焊接工艺参数进行平板表面堆焊实验的基础上,得出各种参数对焊逢成形的影响。焊接工艺参数从两方面影响了焊缝质量。一方面,焊接电流、焊接速度和氩气气体流量三个参数合成的焊接热输入影响着焊缝的强度和韧性；另一方面,这些参数的合理匹配才能焊出成形,也就影响到焊缝的抗裂性、对气孔和夹渣的敏感性。这些参数的合理匹配可以减少焊接缺陷，获得优良的焊缝成型。 关键词 低碳钢；氩弧焊；工艺参数；焊缝成型 Abstract The main research low carbon steel argon tungsten arc welding, when welding current, welding speed, argon gas flow rate of process parameters on the effect of weld moulding. Again and again in different welding process parameters adjustment plate surface surfacing experiment, and on the basis of various parameters that influence of every forming butt weld ends. Welding process parameters influence from two respects the welding quality. On one hand, welding current and welding speed and argon gas flow three parameters of synthesis welding heat input affect weld strength and toughness; On the other hand, these parameters to the rational matching the welding forming, also affect weld resistance of porosity, and slag sensitivity. These parameters of the rational matching can decrease the welding defects, obtain good weld moulding. Key words low carbon steel; Argon arc welding; Process parameters; Weld moulding目录 摘要 I Abstract II 第1章 绪论 1 1.1 课题研究的目的和意义 1 1.1.1 氩弧焊的发展状况及应用范围 1 1.1.2 钨极氩弧焊的原理及特点 3 1.1.3 低碳钢的发展情况及在汽车方面的应用 4 1.2 研究内容与意义 5 第2章 实验方法与设备 6 2.1 实验设备 6 2.1.1 WSE-315P 氩弧焊焊机 6 2.1.2 其他设备 8 2.2 实验材料 10 2.2.1 焊接用板材 10 2.2.2 焊接用焊丝 10 2.2.3 保护气体氩气 11 2.2.4 钨极 11 2.3 焊前清理 11 2.4 其他实验因素的影响 12 2.5 金相试样的制备方法 13 2.6 实验方法 13 小结 14 第3章 实验过程及结果分析 15 3.1 焊接电流对焊缝成型的影响 15 3.2 接速度对焊缝成型的影响 18 3.3 氩气流量对焊缝成型影响 20 3.4 钨极对焊接质量的影响 24 小结 26 结论 28 致谢 30 参考文献 31 附录1 32 附录2 35 第1章 绪论 课题研究的目的和意义 钨极氩弧焊是使用钨极作为非熔化电极，使用惰性气体作为保护气的电弧焊方法。钨极氩弧焊的应用广泛，可以用于几乎所有的金属和合金的焊接，比如钢铁材料，有色金属及其合金，以及金属基复合材料等。由于钨极氩弧焊的诸多优点，在焊接低碳钢的时候可以实现高品质的焊接，得到优良的焊缝，而且钨极氩弧焊的可靠性高，可以用于焊接重要构件。其固有的热影响区小、焊接质量高、焊接变形小、抗裂能力强及机械性能好等优点，使其在压力容器、航天、航海、电站、石油天然气管道等有着广泛的应用。在本次设计中我们将在实验中通过调节各种工艺参数以及各种参数间的