合金高铬铸铁的热处理.docxVIP

摘 要??????本文以合金高铬铸铁（KMTBCr8）板材（5.6mm5.6mm53mm）为试验材料，进行不同热处理后不同腐蚀介质、不同ph、不同砂浆配比、不同转速下的腐蚀磨损试验。 HYPERLINK javascript:; 利用光学显微镜对试样进行基体组织分析、显微组织分析。研究不同热处理工艺及不同腐蚀磨损条件对KMTBCr8腐蚀磨损性能的影响，并分析不同热处理工艺及腐蚀条件下KMTBCr8腐蚀磨损的规律[1]。??????研究发现，KMTBCr8的热处理工艺对其腐蚀磨损性能有影响，铸态的KMTBCr8耐腐蚀磨损性能最好；相同回火温度下，淬火热处理温度越高，KMTBCr8耐腐蚀性越差；相同淬火温度下，KMTBCr8试样低温回火的耐腐蚀磨损性能优于三次高温回火。在其他热处理工艺及腐蚀条件都相同时，中性砂浆中KMTBCr8的表面锈蚀最严重，碱性砂浆次之，酸性砂浆中KMTBCr8的锈蚀最轻。在相同腐蚀磨损条件下，高转速比低转速的失重量要多。??????????????????关键词：合金高铬铸铁；热处理；腐蚀磨损；组织形貌????????????????????????????????????????????????????????Abstract?????? This paper, taking high chromium cast iron alloy plate (5.6mm x 5.6mm x 53mm) as experiment material, respectively in different heat treatment, different corrosive medium, different ph, different cement mortar ratio, different speed of the corrosion wear test . Using Zeiss electron modern analysis methods, the research discusses the heat treatment process and different corrosion wear conditions affect the performance of KMTBCr8 corrosion and wear, and analyze the different heat treatment process and the abrasion performance of the corrosion conditions and corrosion KMTBCr8 relationship; For the material in the actual system theoretical foundation for the safe use. The main research contents include : matrix organization analysis, the morphology and microstructure analysis.??????On the basis of the successful preparation of sample heat treatment, first of all the groups were compared before and after heat treatment. Then to study KMTBCr8 by weight-loss method in acid and alkali neutral mortar dynamic law of corrosion wear characteristics. By comparing the samples before and after corrosion wear weight difference, analyzing corrosion wear data record, a series of XY scatterplot smooth.??????The study found that KMTBCr8 heat treatment process on the corrosion and wear properties of influential, the higher the heat treatment temperature, corrosion resistance, the worse, the more serious the surface rust. In the neutral morta