unit3 铸造工艺.ppt

11. Once the part has completely solidified below the eutectic point it may be removed with no concern for final metal properties. At this point the sand is simply broken up, and the part removed. At this point the surface will have a quantity of sand adhering to the surface, and solid cores inside. 11. 一旦零件在共析点以下完全凝固，可以不考虑金属的最后性能而将其取出。这时可以简单地打碎砂型并取出零件，但零件表面会有大量型砂粘附着，内部还有实心的砂芯。 12. A bulk of the remaining sand and cores can be removed by mechanically striking the part. Other options are to use a vibrating table, sand/shot blaster, hand labor, etc. 12.大量的剩余型砂和砂芯要通过机械敲击零件来去除。其它的选择还有采用振动台、喷砂/喷丸