水泥制造若干节能减排技术探讨.pptVIP

少用熟料 提高胶凝材料利用率 初始组成和堆积状态的优化 水化过程的调控 骨料 熟料 辅助性胶凝材料 水化产物层 未水化熟料 辅助性胶凝材料 研究思路 “区间窄分布，整体宽分布” 模型实现密实堆积 三区间模型 五区间模型 研究思路 Mixture proportions of gap-graded blended cements with five fractions Fraction /μm 4 4-8 8-24 24-45 45-80 Content /% 25 11 25 19 20 BBCFF B B C F F Fraction /μm 8 8-32 32-80 Content /% 36 25 39 BCF B C F Portland cement 100% Cement clinker Reference cement 36% BFS + 25% Cement clinker + 39% Fly ash Note: 5% of gypsum dihydrate by mass of cementitious material was added for all the cements in the Table; C, B, F and S represent cement clinker, blast furnace slag, low calcium fly as