聚酯格栅冻循环试验研究.docVIP

冻融循环对S5050聚酯双向格栅拉伸性能的影响 程卫国1 刘丽佳2,3 孙景路 2,3 张 滨2,3 （1. 江苏优凝舒布洛克公司，江苏 南京 210005 2. 黑龙江省季节冻土区工程冻土重点实验室，黑龙江 哈尔滨 150080；3. 黑龙江省水利科学研究院，黑龙江 哈尔滨 150080） Freezing-Thawing Cycle Effect on the Tensile Properties of Polyester Geogrids Cheng Weiguo1 Liu Lijia 2,3, Sun Jinglu,3, Zhang Bin,3 (1.Jiangsu UniSure Block Co.,Ltd,,Jiangsu Nanjing ,China ,210005 2. Heilongjiang Seasonal Frozen Soil Region Engineering Frozen Soil Key Laboratory, Harbin, China, 150080 3. Heilongjiang Provincial Hydraulic Research Institute, Harbin, China, 150080) Abstract: Tensile properties of polyester geogrids were tested in laboratory at the temperature of 20℃。The geogrids were experienced 50 freezing-thawing cycles. Through the experimental research on the tensile properties of polyester geogrids ,the ultimate bearing capacity, maximum extensibility stress and elastic modulus for different extensibility of geogrids. The test results show that freeze-thaw cycles have little effect on the ultimate extensibility. With the increasing of freezing-thawing cycle, the ultimate extensibility of polyester geogrids and elastic modulus show linear decline.  Key words: polyester geogrids, freezing-thawing cycle, bearing capacity , extensibility ,elastic modulus 摘要：在20℃常温环境下，对经过50冻融循环后的S5050聚酯双向土工格栅进行拉伸试验。研究这些格栅的极限承载力、最大延伸率以及不同延伸率对应的应力值、弹性模量等数据。从试验结果看出冻融循环对材料的极限延伸率影响不大，基本没有变化，冻融循环使材料的极限承载力降低，并随着冻融循环次数的增长，极限承载力和弹性模量均呈线性下降。 关键词：聚酯格栅、冻融循环、屈服强度、延伸率、弹性模量 0、引言 S5050聚酯双向土工格栅的性质均匀稳定、抗拉变形模量大、强度高、韧性好、与土颗粒间的摩擦系数高、连锁作用强,因此在实际工程有着广泛的应用与发展前景。实验室中通常采用直接拉伸试验或在土中的拉拨摩擦试验来研究土工网格栅与土相互作用的界面反应机理,确定网土间的界面特性参数。在北方地区，由于土工格栅加筋挡土墙要经历长期的反复的冻融循环，还要充分考虑冻融循环对土工格栅力学性能的影响。为此本试验室开展了冻融循环条件下聚酯纤维土工格栅的拉伸性能研究，测试冻融循环对S5050聚酯双向格栅极限抗拉强度和延伸率的影响。为今后试验研究中格栅的选择提供理论依据。 1、试验装置、材料 1.1、试验装置 土工格栅冻融循环试验没有相应规范可参照，本次试验极限抗拉强度的测定执行水利部土工合成材料测试规程（SL/T 235-1999）拉伸试验相关规定。 试样冻融循环采用日本东芝公司的冻融循环机，工作温度范围-35℃～+60℃，控制精度：±0.1℃；拉伸试验采用LJ-1000型拉力试验机；数据采集采用DT515数字采集仪；拉力测试采用BLR-1型应力传感器；变形测试采用YHD-100型静态位移传感器。 1.2、试验材料 本次试验材料采用规格为S5050型聚酯纤维土工格栅。其出厂产品检测数据见