辽宁工业大学材料专业毕业论文模板.docVIP

摘 要 本文研究了含 (0.5，1.0，1.5(at.%))的NiAl-Cr(Mo)合金的铸态显微组织和及处理后的组织和。研究结果表明：iAl-Cr(Mo)- Nb合金的显微组织由NiAl、白色的Cr(Mo)两相组成，铸态iAl-Cr(Mo)-0.5Nb合金组织中心的菊花状晶胞最为紧凑，随着Nb含量的增加，菊花中心逐渐分散，共晶胞有粗大的趋势。Cr(Mo)相中，且在胞界处的Cr(Mo)相中更多。经1250℃均匀化热处理后的NiAl-Cr(Mo)-Nb合金iAl-Cr(Mo)-Nb合金iAl-Cr(Mo)；吸铸；显微组织；硬度 Abstract The different Nb content (0.5, 1, 1.5 (at.%)) of NiAl-Cr (Mo)- Nb alloy as-cast microstructure and hardness and its impact on law, and after by 1250 ℃homogenization heat treatment and hardness were studied in this article. The results indicate that three components of the NiAl-Cr (Mo)-Nb alloy microstructure by the black N