泡沫铝研究综述.docVIP

泡沫铝研究综述 班级:材科102班 姓名：吴凯 学号：201004055 指导教师：吕平 泡沫铝研究综述 吴凯 青岛理工大学 摘要：泡沫铝是一种新型的轻质结构功能材料。本文首先介绍在制造泡沫铝的过程中起了至关重要的作用的发泡剂。泡沫铝中气源主要分为H2源和C02气源，氢化物发泡剂应用较为普遍；其次对泡沫铝动态压缩力学性能的实验测量技术进行了总结；另外分析总结了泡沫铝随着气孔孔径的减小，它的力学性能、电磁屏蔽效能、吸音性能的变化；最后，介绍了泡沫铝作为结构材料、功能材料及功能结构一体化材料应用的研究现状。 关键词：泡沫铝；发泡剂；力学性能；冲击荷载；小孔径 Abstract:Foam aluminum is a new lightweight structure and function of materials. This paper describes the process in the manufacture of aluminum foam played a crucial role in the blowing agent. Aluminum foam in the gas source is divided into H2 gas supply sources and CO2, hydrides foaming more general; followed by dynamic compression of aluminum foam mechanical properties of experimental measurement techniques are summarized; another analysis summarizes the aluminum foam with pore size decreases, its mechanical properties, changes in electromagnetic shielding performance, acoustic performance; Finally, the research status of aluminum foam as a structural material, structural and functional integration of functional materials materials applications. Keywords:Foam aluminum；Vesicant；Mechanical Properties；Impact load；Small Aperture 引言 泡沫铝是一种新型的轻质结构功能材料，粉末冶金法是一种制备泡沫铝的重要的方法。在泡沫铝内部含有大量分布可控的孔洞，并以孔洞作为复合相的新型复合材料，具有良好的吸能、减震、缓冲、隔音吸声、隔热、电磁屏蔽、质量轻、高比能等优良的物理和力学性能。另外，研究小孔径泡沫铝对泡沫铝的发展有重要意义，当泡沫铝气孔细化到lmm左右时，可分散细化缺陷，使泡沫铝的结构均匀性提高，而泡沫铝孔结构的均匀化可使其形变的不均匀性降低。研究表明，平均孔径的减小可以使泡沫铝力学性能、能力吸收性能等得到提升。因此，研究小孔径泡沫铝、全面提升泡沫铝性能是当今泡沫铝的重点研究方向之一。正因为泡沫铝有如此多有意的性能，近些年来它在航空航天、汽车、船舶、建筑、装潢、环保、医药等领域被广泛使用。 泡沫铝发泡剂 铝的熔点为660℃，通常低温发泡剂不适合金属铝的发泡。在泡沫铝的生产中应用较多的是无机类热分解型发泡剂。概括起来主要是氢化物型和碳酸盐型。 1．1氢化物发泡剂 在众多的氢化物中，TiH2和ZrH2被认为是最佳的发泡剂[1]，原因是它们在400～600℃释放出发泡气体——氢气，这与铝金属的熔点(660℃)和铝合金的熔点(577℃)比较接近[1]。工业生产中，由于成本和资源等因素，TiH2应用比较普遍，因此国内外发泡剂研究通常集中在TiH2方面。可以利用未经处理的TiH2所释放的氢气在铝熔体中直接发泡，Banhart[2]发现TiH2在氩气保护下加热到390℃开始缓慢地释放氢气，释气过程可分为3个阶段：快速分解阶段、匀速分解阶段和减速分解阶段。然后当温度达到铝或者铝合金熔点以上时，TiH2分解产生的氢气就会在熔融铝或者铝合金内形成无数气泡，冷却这种金属即得到泡沫铝。东北大学先进材料制备中心的姚广春教授采用这种方法制备泡沫铝，以氢化钛作为发泡剂[3]，现在已能批量生产泡沫铝材，并申请了国家发明专利[4]。 1．2碳酸盐发泡剂 V．Gergely在铝金属熔体中加入3