室外花岗岩防碱处理.docVIP

室外花岗岩防碱处理 　　摘要：园林行业中地面、水景、景墙等采用花岗岩已普及，其中湿贴法具有施工简便，价较低的优点，为施工中主要方法。在室外石材景墙、水景、花池等使用后不久就容易出现不同程度的泛碱，影响园林景观的整体观感，未能显示出石材装饰应有的价值。针对这种状况，要从以下几方面来探讨。 　　关键词：园林；室外花岗岩；防碱处理 　　Abstract:In the landscape industry ,ground, waterscape,such as landscape wall which are adopted of granite has been universal.The wet stick method which is the main method for construction in these has simple construction and low price advantages. In outdoor, wall sign, water, such as lotus pond which are made of stones are easy to appear the different degrees of whiskering after shortly using,to affect the landscape overall impressions.Then they fail to show the value of decorative stone. According to this situations, we should discuss from the following several aspects . 　　 Key words: Landscape； Outdoor granite； Prevent alkali treatment 　　中图分类号：K928.73文献标识码：A文章编号： 　　 　　引言： 　　天然石材以其自然庄重、色彩绚丽及较好的抗风化稳定性、耐磨性、耐酸碱性等特点，被建筑师逐渐认识并广泛采用于建筑物的室内、外墙面装饰，极大地突出了建筑的艺术效果。天然石材的安装施工有干挂法和湿贴法，其中湿贴法具有施工简便，造价较底的优点，但也比较容易产生一些质量通病，突出的一点即是石材表面泛碱现象，产生泛碱后的墙面“水印”斑斑，去之无效，拆之亦难，极大地破坏了建筑装饰效果。为此，分析泛碱成因和作相应的预防措施具有重要意义。 　　 　　1．泛碱现象 　　泛碱是花岗岩饰面建筑物表面的一种常见的病害，根据其不同成因和表现方式：有泛霜、泛白、析白、起霜、墙身和装饰面侵蚀等多种叫法。是土、土坯、砖体、水泥、砂浆、混凝土、砌体、瓷砖、涂料等建筑材料的内可溶性盐碱随温度、湿度等外部环境的变化，在吸收水分、水分迁移、水分蒸发过程中随着物理、化学变化的发生而使原建筑材料破坏的一种病害现象。侵蚀破坏的程度也有很大的差异，常见的有返潮、起泡、粉化、起鼓、空鼓、开裂、剥落、发霉、结晶等现象。 　　 　　2．泛碱产生原理 　　泛碱现象的产生有内部和外部两种因素。 　　内部因素，主要是建筑材料存在可溶性的盐类和碱类物质： 　　(1)石材内含Ca2+ 等物质，如大理石等石材的主要成分是碳酸钙占58%以上，当受到大气中的二氧化硫(SO2)及水分作用时，其表层起化学变化即转化为石膏，使其很快失去光泽?并变得疏松多孔。花岗石的主要成分是氧化硅?并含有部分的氧化铝、氧化钙、氧化铁等成分。当氧化铁含量较多时?其石材表面易出现锈斑。 　　(2)大理石及花岗石从微观上观察,其结构组成之间存在着不规则的空隙，花岗岩细孔率为0.5%~1.5%，大理石细孔率为0.5%~2.0%，抗渗性能不如普通水泥砂浆，花岗岩的吸水率0.2%~1.7%时较低的，水仍可通过石材中的毛细管渗入面传到另一面。天然石材的这种特性及毛细孔的存在，为粘结材料中的水、碱、盐等物质的渗入和析出并形成泛碱提供了通道。 　　外部因素，可认为是由于基层材料具有一定的渗透性，当水分从材料表面向内部渗透后，将可溶性物质溶解，而当材料干燥时，水分由内向外发生迁移，将可溶性物质携带到材料表面,随着表面水分蒸发，白色的可溶性物质留在表面，即产生泛碱现象。其原因如下： 　　(1)水泥砂浆的析碱性。 　　(2)水的渗入。由于外墙接缝用水泥细砂砂浆勾缝?令防水效果差;地面水(或潮湿)沿墙体或砂浆层侵入石材板。 　　3．产生的条件 　　(1)使用材料中的碱，它的来源可以是水泥、骨料、外加剂也可以是水和饰面材料。 　　(2)水是泛碱现象产生的来源与介质。 　　(3)面层装饰材料的缝隙及毛细孔是碱接触空气和水的一