镁合金的表面处理镁合金的表面处理.doc

镁合金汪铸件的表面处理 清华大学机械丁程系 曾大本 张鹏 摘要：按照表面成膜过程中有无外加电压作用，将现有镁合金压铸件的表面处理技术归纳为化学成膜技术和阳极氧化成膜技术二大类。分别介绍了化学成膜技术中的铬化处理、磷化处理、锌置换处理、化学腐蚀处理等4类表面处理技术和阳极氧化成膜技术中的常规阳极氧化、等离子体微弧阳极氧化等2类表面处理技术，同时还简要地介绍了作者新近开发的镁合金压铸件交流等离子体微弧氧化处理技术，论述了上述各种技术的特点，总结了在各种表面处理过程中获得高质量膜层应该注意的关键问题，并明确了镁合金压铸件表面处理 技术今后的发展方向。 关键词：镁合金压铸件 表面处理 关键问题 发展方向 ABSTRACT ： The existing surface treatment technology of magnesium alloy die casting were divided into two groups such as chemical coating and anode coating according to whether the voltage being exerted during coating。 The four types of surface treatment technology such as chromate treatment， phosphate treatment， zinc displacement treatment and chemical corrosion treatment in chemical coating and two types such as conventional anode coating and plasma microarc anode coating in anode coating were introduced together with the alternating current plasma microarc oxidization coating which was developed by the author recently The characteristics of these kinds of technology were discussed． The critical problems for good coat in the process of these kinds of surface treatment were summarized。 The development directiOn of surface treatment technology of magnesium alloy die casting was determined。 Key Works：Magnesium Alloy Casting，surface Treatmcnt，CriticaI PrOblem Development Direction 能源危机与环境污染问题的日益突出，使得符合“综合性能优良、可近终形加工、可回收”材料发展方向的镁合金脱颖而出，成为本世纪最受亲睐的一种应用材料。在目前和今后相当长的一段时期内，高效、节能的镁合金压铸件仍将是镁合金的主要应用产品。由于镁的 负电性强（-2.36V SCE），在大气中的耐蚀性极差，所以在使用前必须对镁合金压铸件根据具体要求进行适当的表面处理。在镁合金压铸件的生产成本中，表面处理这部分就占40％左右，因此表面处理对镁合金压铸件的生产和应用至关重要。目前，镁合金压铸件的表面处 理研究不尽相同，不象铝合金表面处理那样成熟和规范，这在一定程度上制约了镁合金压铸件的应用，本文拟对现有的镁合金压铸件的表面处理技术进行简要的归纳，并分析其关键技术问题和发展方向。 一、镁合金压铸件的表面处理技术 镁合金压铸件的表面一般需要依次进行预处理（清理、脱脂、酸洗等）、镀膜、涂装（喷漆、喷塑、镀金属等）等处理“。通常所说的镁合金压铸件的表面处理指的是镀膜这道工艺，其主要作用是在压铸件表面形成与油漆、塑料或金属附着性能好的具有耐腐蚀性的保护膜层。目前，在镁合金压铸领域中主要采用的是湿法表面处理方法。也就是，使用处理溶液进行的表面处理方法。现有的表面处理技术不尽相同，我们根据