用水电比拟法测定高炉内渣铁通过 焦层流速分布的研究 傅世敏　陈　星　周国凡 (武汉冶金科技大学) 摘　要　采用水电比拟法对高炉下部渣铁通过焦层的速度分布进行了测定，并将测定结果与有限差分法的计算结果进行比较，结果表明，二者数值误差在5 %以内。该法投资省，设备简单，测定准确度高。关键词　渣铁流　速度分布　中心焦　水电比拟法 EXPERIMENT ON VELOCITY DISTRIBUTION OF SLAG ANDHOT METAL FLOW PASSING THROUGH COKE LAYER INBLAST FURNACE WITH ELECTRO-HYDRODYNAMICANALOGUE METHOD FU Shimin　CHEN Xing　ZHOU Guofan (Wuhan Metallurgical University of Science and Technology) ABSTRACT　The velocity distribution of slag and hot metal flow passing through coke layer in the lower part of blast furnace has been measured with Electro-hydrodynamic analogue method.The measured results were compared with the results calculated by limited differentiation method.The difference between them is less than 5 %.This method is of low investment,simplicity and high accuracy.KEY WORDS　slag and hot metal,velocity distribution,deadman,Electro-hydrodynamic method 　　渣铁在高炉下部通过焦层的流动是气—固—液三相流，其特性的研究是一个十分困难的问题，不可能直接在高炉内测定。为了精确控制高炉冶炼过程，掌握和计算渣铁在炉内通过焦层流速的分布又十分必要，在水力学渗流理论的启发下，采用水电比拟法进行了这方面的尝试。 1　水电比拟法的理论基础 　　根据水力学中的渗流理论，液体在孔隙介质中的流动称为渗流。为研究渗流中的流速分布，常用渗流简化模型的处理方法，即在渗流模型中定义渗流流速u＝ΔQ/ΔA，ΔQ是通过微小过水断面ΔA的渗流量，同时将渗流看作是在连续空间内的连续介质流动，渗流运动的基本规律是达西(Darcy)定律，即 u＝-KDh/Ds［1］ 式中　K——渗流系数；　　Dh/Ds——水力坡度，单位流程的水头损失［1］。　　高炉内渣铁通过焦柱孔隙的流动可视为通过透气性不均匀的充填层中的粘性流动，此时充填层中的流速矢量亦由Darcy定律确定，即 式中　K——水力学传导系数；　　ψ——水力学势。　　因此可以用研究渗流的方法来研究高炉下部(湿区)渣铁通过焦炭空隙的流动规律，又由于电流与渗流现象之间有着比拟关系(表1)，电场中的电位与渗流场中的水位(H)都满足拉普拉斯(Laplace)方程。因此可通过对电流场电量的测定来研究渗流场，电场中的等位线相当于渗流场中的等势线(等水头线)，有了等势线即可作出流线图，按流网特性可绘出流速图，从而求出流速的分布值。这种通过对电流场的电学量的量测来解答渗流问题的一种研究方法称为水电比拟法。根据水电比拟法，只要用导电材料做成的模型与渗流区几何相似，边界条件相似，导电系数与渗流系数相似，那么通过电场中量测的等位线即为渗流场中的等水头线。 表 1　渗流场与电流场的相似关系Table 1　Analogue relation between flow premeable field and electric current field 电流场 渗流场 电位U 水头H 电导系数σ 渗流系数K 电流密度i 渗流流速u 欧姆定律 达西定律 电位服从拉普拉斯方程 水头服从拉普拉斯方程 电流强度I 渗流量Q 电流线长度L 渗径长度L 电场强度E＝(U1-U2)/L 渗流水力坡度J＝(h1-h2)/L 2　水电比拟法测定渣铁流过高炉下部焦层的速度　　根据高炉内渣铁生成的部位，着重测定了渣铁经炉腰和炉腹通过焦层的流速分布，即图1中的E区(焦炭疏松区)和C区(中心焦区)。　　为提高测定结果的精度，在选择模拟铁水和炉渣的导电液时，应保证模拟铁水、炉渣、焦炭的模拟料与高炉内铁水、炉渣、焦炭密度比相等，高温下炉渣的密度ρs为2.