聚苯乙烯负载氨基葡萄糖树脂的合成及其对硼的吸附研究.doc

聚苯乙烯负载氨基葡萄糖树脂的合成及其对硼的吸附研究 齐风佩1，莫勇权1 (1 湖南城市学院化学与环境工程学院，湖南 益阳 413000) 摘 要：以氨基葡萄糖和聚苯乙烯为原料合成新的螯合树脂，检测了螯合树脂的氯含量和红外光谱；然后利用氨基葡萄糖螯合树脂与硼的螯合性质，通过实验研究其对硼的吸附能力，并研究了温度、时间等影响螯合树脂吸附的因素。根据热力学有关原理，计算出树脂吸附硼的热力学数据，从而得出树脂对硼的吸附效果。结果表明：合成的螯合树脂对硼有一定的吸附效果；较高温度有利于吸附，为吸热反应；ΔG小于0，吸附过程可以自发的进行。 关键词：聚苯乙烯；氨基葡萄糖；硼螯合树脂；吸附 中图分类号：O636.1 文献标识码： 文章编号： Synthesis of Polystyrene Supported Glucosamine and Its Adsorption Properties for Boron QI Feng-pei1, MO Yong-quan1 (1 College of Chemistry and Environmental Engineering, Hunan City University HunanYiyang 413000) Abstract: A new chelating resin was synthesized using glucosamine and polystyrene as material, the infrared spectra and contents of chlorine were detected. The adsorption for boron was studied by using the chelating properties of glucosamine toward boron. The temperature and time of chelating resin for boron adsorption were studied. It was also measured the adsorption isotherms of boron adsorption at different temperature, and the adsorption mechanism and capacity was discussed according to the relationship of thermodynamic function. The results showed that: the resin exhibited high adsorption for boron; higher temperatures was favorable to adsorption, this reaction was an exothermic reaction; ΔG was less than 0, so the adsorption process could be spontaneous. Key words：polystyrene; glucosamine; boron chelating resin; adsorption 1 前言 由于易分解的高品位硼酸盐矿的储量随着硼矿资源的大量消耗而日益减少，世界各国对含硼水溶液的开发十分重视。我国盐湖蕴藏着丰富的硼资源，约占我国硼储量的40%，如能从盐湖水中提取硼，则会产生巨大的经济效益[1]。国外一般采用酸化结晶法和萃取法从水中提取硼[2]。酸化结晶法存在流程复杂、硼酸回收率低、提取过程中盐酸和其它添加剂返回母液造成对盐湖的污染等缺点；萃取法虽然提高了硼的回收率，但是生产成本高。螯合树脂吸附提取硼具有流程简单、操作方便、无污染等特点，螯合树脂相中的螯合配体能与硼离子酯化反应形成稳定的螯合物，对硼有高选择性，因此螯合树脂吸附法提取盐湖卤水中的硼具有广阔的应用前景[3]。本文主要利用氨基葡萄糖的氨基和多羟基的性质，将氨基葡萄糖支载在聚苯乙烯微球上，得到一种含多羟基化合物的树脂，利用硼与羟基化合物的络合作用，研究其对硼的吸附性能。利用这种聚苯乙烯负载氨基葡萄糖树脂在提取硼方面将取得很好的效益，具有良好的应用前景[4]。 2 实验部分 2.1 主要仪器与试剂 UV-3010型紫外分光光度计(日本)；WQF-310红外吸收光谱仪（北京第二光学仪器厂）；SHA-B型恒温振荡器（常州澳华仪器有限公司）；硼酸（AR 长沙分路口塑料化工厂）；N,N-二甲基甲酰胺（AR 天津市恒兴化学试剂制造有限公司）；抗坏血酸（AR 广州化学试剂厂）；甲亚胺-H（BS）