不同表面处理方式在复合树脂再修复技术中的对比研究.docVIP

不同表面处理方式在复合树脂再修复技术中的对比研究 　　[摘要]目的：探讨酸蚀-冲洗、一步法、两步法自酸蚀粘结以及硅烷偶联剂结合以上三种粘结技术对3MZ350老化复合树脂再修复粘结强度的影响，为临床应用提供参考。方法：制作50个树脂条样本，抽取7个为空白对照组不做任何处理，剩余随机分成六个实验组，并进行表面粘结处理，（N=6，n=7）。对完成的试件进行微拉伸检测，并做统计学分析。扫描电镜观察实验组试件表面处理后的粘结面形态。结果:实验组中，硅烷偶联剂+二步法自酸蚀的粘结强度最大（58.73±0.12）MPa，酸蚀-冲洗的粘结强度最小（45.22±0.45）MPa。实验组与对照组比较有统计学意义（P＜0.05）。结论：硅烷偶联剂联合二步法自酸蚀的粘结强度最大，有利于临床老化复合树脂再修复技术的利用。 　　[关键词]复合树脂再修复；硅烷偶联剂；酸蚀；粘结强度 　　[中图分类号]R783 [文献标识码]A [文章编号]1008-6455（2014）05-0397-05 　　 　　The comparative study on Different surface treatments in composite resin restoration techniques 　　WANG Ben-cai,LI Hai-ying,WANG Jian-ping,LIU Shuang,ZHANG Jia-xi,YANG Yu-juan 　　(The Second Department of Endodontics,Affiliated Stomatology Hospital,Jiamusi University,Jiamusi 154007,Heilongjiang,China) 　　 　　Abstract: ObjectiveTo investigate the etching-rinse,one-step,two-step self-etching adhesive and bonding silane coupling combining the above three techniques,for 3MZ350 then repair the aging effects of composite resin bond strength to provide reference for clinical applications.MethodsMaking a total of 50 samples of the resin pieces,extracted five blank control group,no treatment,and the remaining were randomly divided into six experimental groups,and surface adhesion treatment,(N=6,n=7).Specimens were completed on microtensile testing,and do statistical analysis. Scanning electron microscope specimens of each group after the surface treatment adhesive surface morphology.Results In the experimental group,a silane coupling agent+two-step self-etching adhesive systems micro surface treatment tensile strength max (58.73?.12)MPa,etching-surface treatment rinse adhesive systems Micro Tensile strength Min (45.22?.45)MPa. Experimental group and control group was statistically significant(Pto＜0.05).ConclusionSilane coupling joint two-step self-etching adhesive surface treatment system maximum bond strength,is conducive to clinical aging composite resin and then repair the use of technology. 　　Key words:repair composite resin;si